The Particle Size distribution of Cement Binder and Rheological Properties of Paste

시멘트 혼합재의 입도분포와 페이스트 유동특성

  • Received : 2011.05.30
  • Accepted : 2011.06.30
  • Published : 2011.06.30

Abstract

This study examined rheological properties of blast furnace slag and ash paste that are widely used as cement concrete for mineral admixture in current. In that way rheological properties of the paste of mineral admixture only was examined. The result of this study were as follow: In order to analyze that the rheological properties of the mineral admixture only, fine particles were produced with grinding machine to 3 particle sizes. These powders in general from the result of comparison with and analysis of rheological properties and the coefficient n and De values. The result that ash powder was higher in plastic viscosity and yield stress than Slag powder, and with the same n value, ash powder showed higher plastic viscosity and yield stress than Slag powder. But Slag powder in particle size distribution showed a sensitive tendency on changing in rheological properties.

본 연구에서는 현재 시멘트 콘크리트 혼합재로서 널리 사용되고 있는 고로수쇄 슬래그와 애쉬의 페이스트 유동특성을 파악하였다. 그 방법으로 혼합재 단독을 사용한 페이스트의 유동특성을 파악하여, 아래와 같은 결론을 얻을 수 있었다. 혼합재 단독의 페이스트 유동특성을 시험하기 위하여, 3종류의 분쇄기를 사용하여 3가지 입도로 분쇄된 분말을 제조하였다. 이 분말을 Rosin-Rammler 분포식을 사용하여 얻은 계수 n 값과 De 값을 유동특성과 비교 분석한 결과에서, 일반적으로 같은 입경 크기 일 때 Ash 분말이 Slag 분말보다 소성점도 및 항복응력이 높았으며, 또한 동일 n 값에서 Ash 분말이 Slag 분말 보다 비교적 높은 소성점도와 항복응력을 나타내었으나, 입도분포 폭의 변화에는 Slag 분말이 Ash 분말 보다 민감한 유동특성의 변화 경향을 나타내었다.

Keywords