Abstract
The objective of this paper is to evaluate the performance of low $CO_2$ asphalt binder properties using LEADCAP$^{(R)}$(Low Energy and Carbon Asphalt Pavement) additive as function of various aging methods such as RTFO(Rolling thin film oven), Ultraviolet(UV) lay. In order to simulate the short-term aging of asphalt binder that occurs during the hot-mixing asphalt process, the Rolling Thin Film Oven(RTFO) was used. Asphalt binder using LEADCAP$^{(R)}$ is prepared by addition of a photoinitiator activated by ultraviolet lay. The mechanical and rheological properties of the asphalt binder were estimated using UTM(Universal Testing Machine) and DSR(Dynamic Shear Rheometer). The test results showed that the asphalt binder using LEADCAP$^{(R)}$ additive was improved the rutting resistance at testing temperature ($70^{\circ}C$) and increased tensile strength at low temperature. Also, Thermal analysis shows that the Melting Point(Tm) of asphalt binder using LEADCAP$^{(R)}$ additive was constant although the asphalt binder was aged by Ultraviolet.
본 연구의 목적은 중온화 첨가제(LEADCAP$^{(R)}$)를 사용한 중온 아스팔트 바인더의 노화 방법에 따른 물성 변화 특성을 평가하고자 하였다. 아스팔트 바인더의 노화 거동을 모사하기 위해 단기노화인 RFTO를 실시하였으며, 햇빛에 의한 자연 노화 거동을 알아보기 위해 자외선 경화기를 이용하여 자외선에 의한 열화거동을 모사하였다. 이러한 열화 중온 아스팔트 바인더의 역학적인 물성과 유변동학적인 특성을 시험하기 위해서 만능시험기(UTM)과 동적전단유동기를 이용하여 직접인장력과 유변동학적인 거동을 평가하였다. 또한, 열분석 장비를 이용하여 온도에 따른 중온 아스팔트 바인더의 특성을 평가하여, 자외선 노출에 따른 열화가 발생하여도 온도에 따른 물성 변화가 많이 발생하지 않음을 발견하였다. $70^{\circ}C$에서 중온화 첨가제가 첨가한 단기노화 중온 아스팔트 바인더의 경우, PG 등급에서의 고온 등급의 기준값을 만족함을 알 수 있었다. 또한 저온에서 중온 아스팔트 바인더의 인장 특성을 평가한 결과, 인장강도 향상과 함께 인장력이 증가됨을 알 수 있었다.