Adhesion Properties of Low VOC-type Primer Containing Acrylic Modified Tackifier Resin

Acrylic Modified Hydrocarbone Resin을 포함하는 저독성 프라이머의 제조 및 특성

  • Received : 2010.11.06
  • Accepted : 2011.02.12
  • Published : 2011.03.30
Download PDF
⟨ Previous Next ⟩

Abstract

In this study we synthesized low VOC-solvent soluble thermo plastic polyurethane, The effect of chain extender and NCO/OH ratio for properties of thermoplastic polyurethane was investigated. Also, we prepared low VOC-type primer by TPU and acrylic modified tackifier resin. When NCO/OH ratio was 2 or more, TPU was insoluble in low VOC solvent. And peel strength was higher value using polar type tackifier than non-ploar type tackifier.

본 연구에서는 저독성 용제에 용해도가 있는 열가소성 폴리우레탄(TPU, Thermoplastic Polyurethane)을 합성하고 폴리우레탄 합성시 사용되는 사슬연장제 및 NCO/OH 비에 따른 물성 변화를 알아보았다. 또한 합성된 열가소성 폴리우레탄을 이용하여 난접착재질용 저독성 프라이머를 제조하고 접착특성을 알아보고자 하였다. TPU 합성시 r(NCO/OH) = 2.0 이상인 경우에는 폴리올 및 이소시아네이트의 종류에 관계없이, 저독성 용제에 용해도가 저하되는 결과를 나타냈으며, non polar한 구조를 가지고 있는 접착증진제보다는 polar한 구조를 가지고 있는 접착증진제의 접착력이 우수하게 나타났다.

Keywords

References

  1. Z. Wirpsza, Polyurethanes Chemistry Technology and Applications, Ellis Horwood, New York (1993).
  2. G. Oertel, Polyurethane Handbook, Hanser, Cincinnati (1994).
  3. J. Y. K. J. Seo, S. Y. Kwon, J. P. Wu, and H. S. Park, Polymer (Korea), 22, 756 (1998).
  4. C. Hepbum, Polyurethane Handbook, Elsevier Science Publishing Co., New York (1992).
  5. B. Y. Jeong, J. M. Cheon, J. M. Chun, D. M. Mok, and H. M. Lee, Jounal of Adhesion and Interface, 10, 4 (2009).
  6. K. C. Frrish and S. L. Reegen, Advances in Urethane Science and Technology vol. 1-8, Technomic USA (1978).
  7. R. Bonart, Polymer, 20, 1389 (1979). https://doi.org/10.1016/0032-3861(79)90280-5
  8. M. J Han, K. B. Choi, S. H. Kim, and S. H Lee, Polymer (Korea), 7, 6 (1983).
  9. B. Y. Jeong, J. M. Cheon, J. S. Yoo, and J. H. Chun, Journal of Adhesion and Interface, 8 (2007).
  10. S. K. Kim, K. S. Kim, T. K. Kim, and G. J. Oh, Elastomer, 35, 281 (2000).
  11. A. W. McLennaghan and R. A. Petherick, Eur. Polym. J., 24, 1063 (1988). https://doi.org/10.1016/0014-3057(88)90066-3
  12. Y. K. Yang, N. S. Kwak, and T. S. Hwang, Polymer (Korea), 29, 81 (2005).
  13. D. W. Kang, Y, M. Kim, and D. K. Kweon, Polymer (Korea), 22, 4 (1998).
  14. S. H. Shin, B. Y. Jeong, I. D. Chung, N. J. Jo, J. M. Cheon, and J. H. Chun, Jounal of Adhesion and Interface, 11 (2010).
  15. J. M. Cheon, B. Y. Jeong, S. T. Oh, T. K. Kim, and J. H. Chun, Jounal of Adhesion and Interface, 11 (2010).
  16. T. O. Ahn, I. P. Hong, J. H. Kim, and H. M. Jeong, Polymer (Korea), 14, 6 (1990).