APPLICATION OF COLD SPRAY COATING TECHNIQUE TO AN UNDERGROUND DISPOSAL COPPER CANISTER AND ITS CORROSION PROPERTIES

  • 투고 : 2011.03.17
  • 심사 : 2011.05.30
  • 발행 : 2011.12.25

초록

A cold spray coating (CSC) of copper was studied for its application to a high-level radioactive waste (HLW) disposal canister. Several copper coatings of 10 mm thick were fabricated using two kinds of copper powders with different oxygen contents, and SS 304 and nodular cast iron were used as their base metal substrates. The fabricated CSC coppers showed a high tensile strength but were brittle in comparison with conventional non-coating copper, hereinafter defined to as "commercial copper". The corrosion behavior of CSC coppers was evaluated by comparison with commercial coppers, such as extruded and forged coppers. The polarization test results showed that the corrosion potential of the CSC coppers was closely related to its purity; low-purity (i.e., high oxygen content) copper exhibited a lower corrosion potential, and high-purity copper exhibited a relatively high corrosion potential. The corrosion rate converted from the measured corrosion current was not, however, dependent on its purity: CSC copper showed a little higher rate than that of commercial copper. Immersion tests in aqueous HCl solution showed that CSC coppers were more susceptible to corrosion, i.e., they had a higher corrosion rate. However, the difference was not significant between commercial copper and high-purity CSC copper. The decrease of corrosion was observed in a humid air test presumably due to the formation of a protective passive film. In conclusion, the results of this study indicate that CSC application of copper could be a useful option for fabricating a copper HLW disposal canister.

키워드

참고문헌

  1. Nuclear Waste Bulletin No. 14, Nuclear Energy Agency Organization for Economic co-operation and Development, 2000.
  2. C.G. Andersson, "Development of Fabrication Technology for Copper Canisters with Cast Inserts", Technical report TR-02-07, SKB (2002).
  3. H. Raiko, J. P. Salo, "Design Report of the Canister for Nuclear Fuel Disposal", Report 96-13, POSIVA (1996).
  4. Japan Nuclear Cycle Development Institute, "Project to Establish the Scientific and Technical Basis for HLW Disposal in Japan", H12 Report, JAEA (2000).
  5. N. Taniguchi, M. Kawasaki, and M. Naito, "Effect of Sulfide on the Corrosion Behavior of Pure Copper under Anaerobic Condition and Possibility of Super Long Lifetime for Copper Overpacks", JAEA-Research 2007-022, JAEA (2007) (in Japansese).
  6. D.W. Shoesmith, "Assessing the Corrosion Performance of High-Level Nuclear Waste Containers ", Corrosion, 62(8), 703 (2006). https://doi.org/10.5006/1.3278296
  7. M. Pourbaix, Atlas of Electrochemical Equilibria in Aqueous Solutions, Pergamon, 1966.
  8. D.G. Brookins, Eh-pH Diagrams for Geochemistry, Springer-Verlag, 1988.
  9. J. Lee, H.J. Cho, and J. Choi, "Concept of a Korean Reference Disposal System for Spent Fuels", J. Nucl. Sci. Technol. 44, 1565 (2007). https://doi.org/10.3327/jnst.44.1565
  10. Swedish Nuclear Fuel and Waste Management Co., "RD & D Programme 2007", Technical Report TR-07-12, SKB (2007).
  11. W. H. Bowyer, "Design Basis For The Copper/Steel Canister", SKI Report 98:29, SKI (1998).
  12. W. H. Bowyer, "A Study of Defects which Might Arise in the Copper Steel Canister", SKI Report 00:19, SKI (1999).
  13. S.S. Kim, K. S. chun, J. W. Yeon, and J.W. choi, "Corrosion of the Candidate Materials for the Disposal Container of a High-Level Radioactive Waste", J. the Korean Radioactive Waste Society, 23, No. 2, 97 (2006).
  14. B. Kursten, E. Smailos, I.Azkarate, L. Werme, N.R. Smart, and G. Santarini, COBECOMA (State-of-the-art document on the COrrosion BEhaviour of Container Materials), Final report, EUROPEAN COMMISSION, (2003).
  15. U.S. Department of Energy, "Science and Technology Program Plan", DOE/RW-0576, DOE, (2005).
  16. C. G. Andersson, "Test Manufacturing of Copper Canisters with Cast Inserts", Technical report TR-98-09, SKB (1998).
  17. A. Papyrin, "Cold Spray Technology", Advanced Materials & Processes, 49 (2001)
  18. Nuclear Energy Agency, "Engineered Barrier Systems and the Safety of Deep Geological Repositories", ISBN 92- 18498-8, NEA (2003).
  19. C. G. Andersson, P. E., and M Westman, , "Status Report, Canister Fabrication" Technical report TR-04-23, SKB (2004).
  20. T. Aastrup, M. Wadsak, M. Schreiner, and C. Leygraf, "Experimental in situ studies of copper exposed to humidified air", Corrosion Science, 42, 957 (2000) https://doi.org/10.1016/S0010-938X(99)00125-0
  21. K. P. FitzGerald, J. Narirn, G. Skennerton, and A. Atrens, "Atmospheric corrosion of copper and the colour, structure and composition of natural patinas on copper", Corrosion Science, 48, 2480 (2006) https://doi.org/10.1016/j.corsci.2005.09.011
  22. Korea Atomic Energy Research Institute, "High-Level Radwaste Disposal Technology Development", Research report RR-2765, KAERI (2006). (in Korean)
  23. J. Ambrose, R. Barradas, and D. W. Shoesmith, "Investigations of Copper in Aqueous Alkaline Solutions by Cyclic Voltammetry", J. Electroanal. Chem. & Interfacial Electrochem., 47, 47 (1973). https://doi.org/10.1016/S0022-0728(73)80344-4
  24. A. D. Modestov, G. D. Zhou, H. H. Ge, B. H. Loo, "A Study by Voltammetry and Photocurrent Response Method of Copper Electrode Behavior in Acidic and Alkaline Solutions Containing Chloride ions", J. Electroanal. Chem., 380, 63 (1995). https://doi.org/10.1016/0022-0728(94)03577-P
  25. J. Crousier, L. Pardessus, J. P. Crousier, "Voltammetry Study of Copper in Chloride Solution", Electrochim. Acta, 33, 1039 (1988). https://doi.org/10.1016/0013-4686(88)80192-0