Abstract
Glass-ceramics composed of $5Na_2O-36CaO-10TiO_2-xP_2O_5$ could be obtained with $P_2O_5$ content as following procedure: 1) leaching out $Ca_3(PO_4)_2$ crystals between $Ca_3(PO_4)_2$ and $NaTi_2(PO_4)_3$ selectively in 1 N HCl solution for 2 days, and 2) exchanging $Na^+$ ion to $Ag^+$ ion in Ag($NO_3$) solution for 1 day. Scanning electron microscope (SEM) and X-rat diffractometer (XRD) were measured to verify the proper synthesis of glass-ceramics. And anti-bacteria test was accomplished using Staphylococus aureus bacteria. In the results of anti-bacteria test, the bacteria were died perfectly after 3 hours.
$P_2O_5$ 함량에 따른 $5Na_2O-36CaO-10TiO_2-xP_2O_5$으로 구성된 glass-ceramic을 다음과 같은 방법으로 제조하였다: 1) 1 N HCl 용액 내에서 $Ca_3(PO_4)_2$와 $NaTi_2(PO_4)_3$ 간의 $Ca_3(PO_4)_2$ 결정을 2일간 추출하여 제거함. 2) Ag($NO_3$) 용액에서 1일간 $Na^+$ 이온을 $Ag^+$ 이온으로 이온 교환시킴. Glass-ceramic의 합성 여부를 SEM 및 XRD를 이용하여 확인하였다. Staphylococus aureus를 이용한 박테리아 실험 결과 3시간 이후에는 완전하게 박테리아가 제거됨을 확인할 수 있었다.