Abstract
GTAW was carried out to the austenitic 304(STS 304) and 22 APU stainless steels. In this case, difference of the corrosion characteristics of welded zone with STS 304 and 22APU mentioned above was investigated with electrochemical methods. Vickers hardness of weld metal in case of STS 304 (Hv-250) showed a relatively higher value than this of 22 APU(Hv-217). The corrosion current densities of weld metal of 22APU and heat affected zone of STS 304 were observed at the highest value compared to those of other welding zone respectively. This is probably because chromium depletion field due to chromium carbide formed to weld metal of 22APU and to heat affected zone of STS 304 can preferentially easily be corroded with more active anode than other fields. Consequently it is thought that application of the other welding methods like as laser welding or using of the optimum filler metals is necessary to improve the corrosion resistance of welding parts of these steels.
STS304와 22APU 스테인리스강에 가스 텅스텐 아크용접을 하였다. 이 경우 두 강의 용접부의 부식특성을 전기화학적 방법으로 검토하였다. STS304 용접금속의 경도(Hv-250)는 22APU 강(Hv-217) 보다 상대적으로 높은 값을 보였다. 22APU의 용접금속과 STS 304의 열영향부의 부식전류 밀도는 다른 용접부위와 비교하여 각각 높은 값이 관찰 되었으며, 이것은 예민화 온도 영역에 있는 STS 304의 열영향부와 22APU의 용접금속에 형성된 크롬탄화물로 크롬결핍이 더욱 활성태의 양극으로 쉽게 부식된 것에 기인하는 것으로 사료된다. 그리고 이들 두 강의 용접금속과 열영향부는 크롬결핍상태에 있는 입자 사이 경계의 선택부식으로 입계부식을 나타내었다. 결과적으로 다른 용접방법의 적용이나 적절한 용접봉 사용은 두 강의 용접부에 대한 내식성을 개선하기 위해서 필요한 것으로 사료된다.