Abstract
Coal briquette use has dramatically increased because of high oil prices. Hence, it is necessary to develop an environment-friendly recycling technique of the coal briquette ash. The coal briquette ash contains a large amount of an unburned carbon content and a mullite with high thermal property, so it is considered to be used as raw materials of sintered eco-brick. This study aimed to investigate on how the unburned carbon affects properties of the sintered eco-brick. The eco-brick was mixed with the ratio of 50 wt% coal briquette ash having the unburned carbon 10.5 wt% and 50 wt% cullet, then being sintered at $950^{\circ}C$, which of the compressive strength was in line with the first class of the sintered clay brick standard(KS L 4201). In particular, the compressive strength of the sintered eco-brick was equal to the first class of the KS L 4201 despite the increase of mixing ratio for coal briquette ash with 1.0 wt% unburned carbon to 70 wt%.
최근 고유가 시대로 접어들면서 연탄의 사용량이 급격하게 증가하고 있어 이때 발생되는 연탄재의 친환경적인 순화자원화 기술개발이 필요하게 되었다. 연탄재에는 가연성분인 미연탄소와 고온열적특성이 우수한 뮬라이트 성분이 다량 함유되어 있어 소성 에코벽돌의 원료로 적합하다고 판단된다. 이 연구의 목적은 연탄재에 함유되어 있는 미연탄소가 소성 에코벽돌의 특성에 어떠한 영향을 미치는 가를 파악하는데 있었다. 미연탄소 함량 10.5 wt%인 연탄재 50 wt%와 폐유리 50 wt%의 배합비율로 제조한 에코벽돌을 $950^{\circ}C$로 소성한 시험체의 압축강도는 소성 점토벽돌 국내규격(KS L 4201)의 1종 규격에 해당하였다. 특히, 미연탄소 함량이 1.0 wt%인 연탄재의 배합비율을 70 wt%까지 증가시켜 제조한 소성 에코벽돌 시험체의 압축강도는 소성 점토벽돌 1종 규격에 해당하였다.