Abstract
The purpose of this study is to examine the effect of variations in the mix rate of PVA fiber and the replacement ratio of non-sintering Hwangtoh on non-sintering Hwangtoh mortar and concrete mixed with PVA fiber. For water to binder ratio, mortar and concrete were both 50%, and PVA fiber mix rate was 0% and 0.3%. The replacement ratio of non-sintering Hwangtoh was 0, 25, 50 and 75(%) for mortar, and 0, 15, 30 and 50(%) for concrete. The properties of the mortar and concrete were compared and analyzed in 4 different levels, and the results can be summarized as follows. The replacement ratio of 30% of the non-sintering Hwangtoh, and the PVA fiber mix rate of 0.3% is determined to result in concrete of high quality, including strength and fluidity, and crack control by plastic shrinkage.
본 연구에서는 PVA섬유를 혼입한 비소성 황토 모르타르 및 콘크리트에 있어, PVA 혼입율 및 비소성 황토의 치환율에 따른 영향을 검토하기 위하여 계획한 실험으로서 물-결합재비는 모르타르와 콘크리트 동일하게 50%, PVA혼입율은 0, 0.3(%)로 하였으며, 비소성 황토 치환율은 모르타르의 경우 0, 25, 50, 75(%), 콘크리트의 경우 0, 15, 30, 50(%)로 각각 4수준에 따른 모르타르 및 콘크리트의 성상을 비교 분석하여 결과를 종합하면 다음과 같다. 비소성 황토의 치환율 30%, PVA섬유 혼입율은 0.3%를 사용할 때 강도 및 유동성, 소성수축에 의한 균열제어 등 양질의 콘크리트를 만들 수 있을 것으로 판단되며, 향후 친환경 콘크리트 시공시에 활용이 가능 할 것으로 사료된다.