Abstract
As the competition of acquiring foreign resources of advanced countries and developing countries intensifies, South Korea which imports most of the mineral resources, started to re-develop domestic mines for molybdenite ore, in order to secure stable natural resources and decrease foreign currency expense. In this study, as a result of performing XRD and composite analysis on Dongwon NMC's (the sole producer of molybdenite ore in Korea) final concentrate(Mo 50.4%), Quartz, Grossular and Hedenbergite exists as impurities and size analysis showed that in relative coarse particle range of 60~140 mesh was formed with high grade over 57% Mo. Also, a test was performed to confirm the possibilities of increasing the grade and recovery of Dong won NMC's final ore. As a result, Mo 58.6% ($MoS_2$ 97.83%) was obtained with 87.47% recovery at a condition of 15 minutes grinding time, Kerosene as collector 0.1 l/ton, AF as Frother 65 7.2 l/ton, wash water of 630 ml/min and air flow rate of 1,197 ml/min.
신흥개발국과 선진국의 해외자원 확보 경쟁이 심화되는 가운데 대부분의 광물자원을 수입하고 있는 우리나라는 안정적인 자원확보 및 외화지출을 줄이기 위해 국내에 부존되어 있는 몰리브덴광 등을 재개발하기 시작하였다. 본 연구에서는 현재 국내에서 유일하게 몰리브덴광을 생산하고 있는 (주)동원NMC의 최종정광(Mo 50.4%)을 대상으로 XRD 및 성분분석 결과 석영과 Grossular, Hedenbergite 등이 불순문로 존재하였으며, 입도분석 결과 60~140 mesh의 비교적 조립질 구간에 Mo 57% 이상의 고품위로 구성되어 있음을 확인하였다. 또한, (주)동원NMC의 최종정광(Mo 50.4%)의 고품위 가능성 및 실수율 향상 가능성을 확인하기 위해 실험을 실시하였다. 그 결과 마광시간 15분, 포수제 Kerosene 0.1 l/ton, 기포제 AF 65 7.2 l/ton, 세척수량 630 ml/min., air flow rate 1,197 ml/min.의 조건에서 Mo 58.6% ($MoS_2$ 97.83%)의 산물을 87.47%의 실수율로 얻을 수 있었다.