Autogenous Shrinkage and Fundamental Properties of the High Strength Mortar Containing Waste Vegetable Oil

폐식용유를 사용한 고강도 모르터의 자기수축 및 공학적 특성

The objective of this paper is to explore the possibility of reuse of waste vegetable oil (WO) as an autogenous shrinkage reducer for high strength concrete and to compare the amount of autogenous shrinkage of the mortar using existing shrinkage reducing agent(SR) and expansive additives(EA). According to test results, as the dosages of WO increased, flow value exhibited to decrease, while the use of SR increased flow value. For the effect of WO on strength, although the use of SR and WO resulted in a slight decrease in compressive strength at early age, at 91 days they had similar strength level of the plain mixture. For autogenous shrinkage, as expected, the addition of WO, SR and EA resulted in a decrease of autogeneous shrinkage considerably especially, WO had superiority in autogenous shrinkage reducing effect compared with the case of SR and EA.

본 연구에서는 폐식용유에 의한 고강도 모르터의 기초적 및 자기수축 특성을 팽창재, 수축저감제를 사용한 경우와 비교 분석하였는데, 그 결과는 다음과 같다. 유동성은 폐식용유의 경우 Plain에 비해 다소 적게 나타났고, 치환율의 증가에 따라서도 감소하였다. 반면, 수축저감제는 Plain보다 증가하는 것으로 나타났고, 팽창재는 치환율의 증가에 따라 증가하는 경향을 나타내었다. 압축강도의 경우 폐식용유 및 수축저감제에서는 상호 유사한 경향을 나타내었는데, 초기 재령에서는 플레인 배합에 비해 다소 작은 값을 나타내었지만, 재령 91일에서는 거의 유사한 강도를 나타내었으며, 팽창재는 전반 재령에서 모두 Plain보다 높은 강도를 나타내었다. 자기수축 특성을 볼때 수축저감제, 폐식용유, 팽창재 순으로 수축저감효과가 양호한 것으로 나타났는데, 특히 폐식용유의 자기수축 저감효과는 수축저감제와 큰 차이를 보이지 않았고, 팽창재에 비해 양호한 것을 알 수 있었다.