초록
For the fabrication of PMOS and integrated semiconductor devices, B, $BF_2$ and dual elements with B and $BF_2$ can be implanted in silicon. 15 keV B ions were implanted in silicon at $7^{\circ}$ wafer tilt and a dose of $3.0{\times}10^{16}\;cm^{-2}$. 67 keV $BF_2$ ions were implanted in silicon at $7^{\circ}$ wafer tilt and a dose of $3.0{\times}10^{15}\;cm^{-2}$. For dual implantations, 67 keV $BF_2$ and 15keV B were carried out with two implantations with dose of $1.5{\times}10^{15}\;cm^{-2}$ instead of $3.0{\times}10^{15}\;cm^{-2}$, respectively. For the electrical activation, the implanted samples were annealed with rapid thermal annealing at $1,050^{\circ}C$ for 30 seconds. The implanted profiles were characterized by using secondary ion mass spectrometry in order to measure profiles. The implanted and annealed results show that concentration profiles for the ${BF_2}^+$ implant are shallower than those for a single $B^+$ and dual ($B^+$ and ${BF_2}^+$) implants in silicon. This effect was caused by the presence of fluorine which traps interstitial silicon and ${BF_2}^+$ implants have lower diffusion effect than a single and dual implantation cases. For the fabricated diodes, current-voltage (I-V) and capacitance-voltage (C-V) were also measured with HP curve tracer and C-V plotter. Electrical measurements showed that the dual implant had the best result in comparison with the other two cases for the turn on voltage characteristics.