Abstract
Purpose: We investigated the changes of plastic lens after etching of coating films by comparing uncoated lens. Methods: CR-39, middle index and high index lenses of 0 (zero) diopter were etched at $80^{\circ}C$ and room temperature using a coating remover, and then changes of refractive power, transmittance and surface morphology were investigated. Results: There were no differences in refractive power and transmittance between uncoated and etched lenses. The etching rate was similar in both CR-39 and middle index lens, but in the case of high index lens, it was slower and less steady than the others. From the SEM observation of lens surface, etching damage was found out on the surface of etched lens. It was shown the least damage in middle index lens but the most damage in high index lens. Conclusions: If the etching of coating films is demanded on condition that the surface of ophthalmic lenses are not damaged, a using of most adequate coating remover based on lens material should be considered, and a caution for proper etching conditions is required.
목적: 플라스틱렌즈 표면의 코팅막을 식각한 렌즈와 무코팅렌즈를 비교함으로써, 코팅의 식각이 렌즈에 미치는 변화를 연구하였다. 방법: 굴절력이 0 디옵터인 CR-39, 중굴절률, 고굴절률렌즈를 코팅제거제를 사용하여 $80^{\circ}C$와 상온에서 식각하였고, 굴절력, 투과율 및 렌즈 표면의 변화를 조사하였다. 결과: 코팅의 식각으로 렌즈의 굴절력의 변화는 없었으며, 무코팅렌즈와 식각된 렌즈의 광투과율도 거의 차이가 없었다. 식각속도는 CR-39와 중굴절률렌즈에서 비슷하였으나 고굴절률렌즈에서는 느리고, 불규칙하였다. 렌즈 미세 표면을 관찰한 결과 렌즈 표면에 식각으로 인한 손상이 나타났는데, 중굴절률렌즈의 손상이 가장 적었고, 고굴절률렌즈에서 가장 많았다. 결론: 안경렌즈 표면이 손상되지 않도록 코팅막을 식각하려면, 렌즈 소재에 맞는 적합한 코팅제거제가 사용되어야 하며, 적절한 식각조건에 대한 주의가 필요할 것이다.