Preparation and characterization of inexpensive submicron range inorganic microfiltration membranes

  • Nandi, B.K. (Department of Chemical Engineering, Indian Institute of Technology Guwahati) ;
  • Das, B. (Department of Chemical Engineering, Indian Institute of Technology Guwahati) ;
  • Uppaluri, R. (Department of Chemical Engineering, Indian Institute of Technology Guwahati) ;
  • Purkait, M.K. (Department of Chemical Engineering, Indian Institute of Technology Guwahati)
  • 투고 : 2009.12.01
  • 심사 : 2010.02.09
  • 발행 : 2010.04.25

초록

This work presents inexpensive inorganic precursor formulations to yield submicron range symmetric ceramic microfiltration (MF) membranes whose average pore sizes were between 0.1 and $0.4{\mu}m$. Incidentally, the sintering temperature used in this work was about 800 to $950^{\circ}C$ instead of higher sintering temperatures ($1100^{\circ}C$) that are usually deployed for membrane fabrication. Thermogravimetric (TGA) and X-Ray diffraction (XRD) analysis were carried out to evaluate the effect of temperature on various phase transformations during sintering process. The effect of sintering temperature on structural integrity of the membrane as well as pore size distribution and average pore size were evaluated using scanning electron microscopy (SEM) analysis. The average pore sizes of the membranes were increased from 0.185 to $0.332{\mu}m$ with an increase in sintering temperature from 800 to $950^{\circ}C$. However, a subsequent reduction in membrane porosity (from 34.4 to 19.6%) was observed for these membranes. Permeation experiments with both water and air were carried out to evaluate various membrane morphological parameters such as hydraulic pore diameter, hydraulic permeability, air permeance and effective porosity. Later, the membrane prepared with a sintering temperature of $950^{\circ}C$ was tested for the treatment of synthetic oily waste water to verify its real time applicability. The membrane exhibited 98.8% oil rejection efficiency and $5.36{\times}10^{-6}\;m^3/m^2.s$ permeate flux after 60 minutes of experimental run at 68.95 kPa trans-membrane pressure and 250 mg/L oil concentration. Based on retail and bulk prices of the inorganic precursors, the membrane cost was estimated to be $220 /$m^2$ and $1.53 /$m^2$, respectively.

키워드

참고문헌

  1. Balek, V. and Murat, M. (1996), "The emanation thermal analysis of kaolinite clay minerals", Thermochim. Acta., 282-283, 385-397. https://doi.org/10.1016/0040-6031(96)02886-9
  2. Belouatek, A., Benderdouche, N., Addou, A., Ouagued, A. and Bettahar, N. (2005), "Preparation of inorganic supports for liquid waste treatment", Micropor. Mesopor. Mat., 85, 163-168. https://doi.org/10.1016/j.micromeso.2005.06.007
  3. Bouzerara, F., Harabi, A., Achour, S. and Larbot, A. (2006), "Porous ceramic supports for membranes prepared from kaolin and doloma mixtures", J. Eur. Ceram. Soc., 26, 1663-1671. https://doi.org/10.1016/j.jeurceramsoc.2005.03.244
  4. Chakrabarty, B., Ghoshal, A.K. and Purkait, M.K. (2008a), "SEM Analysis and Gas Permeability Test to Characterize Polysulfone Membrane Prepared with Polyethylene Glycol as Additive", J. Colloid Interf. Sci., 320, 245-253. https://doi.org/10.1016/j.jcis.2008.01.002
  5. Chakrabarty, B., Ghoshal, A.K. and Purkait, M.K. (2008b), "Ultrafiltration of stable oil-in-water emulsion by polysulfone membrane", J. Membrane Sci., 325, 427-437. https://doi.org/10.1016/j.memsci.2008.08.007
  6. Chemical Industry news intelligence (2009), http://www.icis.com.
  7. Chen, G., Xing, H.Q.W. and Xu, N. (2008), "Direct preparation of macroporous mullite supports for membranes by in situ reaction sintering", J. Membrane Sci., 318, 38-44. https://doi.org/10.1016/j.memsci.2008.01.034
  8. China Glass Network (2009), http://www.glassinchina.com.
  9. Das, R. and Dutta, B.K. (1999), "Permeation and Separation Characteristics of Supported Alumina and Titania Membranes", Sep. Sci. Technol., 34, 609-625. https://doi.org/10.1081/SS-100100670
  10. DeFriend, K.A., Wiesner, M.R. and Barron, A.R. (2003), "Alumina and aluminate ultra-filtration membranes derived from alumina nanoparticles", J. Membrane Sci., 224, 11-28. https://doi.org/10.1016/S0376-7388(03)00344-2
  11. Falamaki, C., Shafiee, A.M. and Aghaie, A. (2004), "Initial sintering stage pore growth mechanism applied to the manufacture of ceramic membrane supports", J. Eur. Ceram. Soc., 24, 2285-2292. https://doi.org/10.1016/S0955-2219(03)00643-5
  12. Gestel, T.V., Vandecasteele, C., Buekenhoudt, A., Dotremont, C., Luyten, J., Leysen, R., Bruggen, B.V. and Maesc, G. (2002), "Alumina and titania multilayer membranes for nanofiltration: preparation, characterization and chemical stability", J. Membrane Sci., 207, 73-89. https://doi.org/10.1016/S0376-7388(02)00053-4
  13. JCPDS (Joint Committee for Powder Diffraction Studies) (1997), Powder Diffraction File of Inorganic Phases, International Center for Diffraction Data, Swarthmore, PA, USA.
  14. Jedidi, I., Khemakhem, S., Larbot, A. and Amar, R.B. (2009), "Elaboration and characterization of fly ash based mineral supports for microfiltration and ultrafiltration membranes", Ceram. Int., 35, 2747-2753. https://doi.org/10.1016/j.ceramint.2009.03.021
  15. Khemakhem, S., Larbot, A. and Ben Amar, R. (2009), "New ceramic microfiltration membranes from Tunisian natural materials: Application for the cuttlefish effluents treatment", Ceram. Int., 35, 55-61. https://doi.org/10.1016/j.ceramint.2007.09.117
  16. Masmoudia, S., Larbot, A., Feki, H.E. and Amara, R.B. (2007), "Elaboration and characterisation of apatite based mineral supports for microfiltration and ultrafiltration membranes", Ceram. Int., 33, 337-344. https://doi.org/10.1016/j.ceramint.2005.10.001
  17. Mulder, M. (1991), Basic Principles of Membrane Technology, Kluwer Academic Publishers, Dordrecht.
  18. Nandi, B.K., Uppaluri, R. and Purkait, M.K. (2008), "Preparation and characterization of low cost ceramic membranes for microfiltration applications", Appl. Clay Sci., 42, 102-110. https://doi.org/10.1016/j.clay.2007.12.001
  19. Nandi, B.K., Uppaluri, R. and Purkait, M.K. (2009), "Effects of dip coating parameters on the morphology and transport properties of cellulose acetate-ceramic composite membranes", J. Membrane Sci., 330, 246-258. https://doi.org/10.1016/j.memsci.2008.12.071
  20. Potdar, A., Sukla, A. and Kumar, A. (2002), "Effect of gas phase modification of analcime zeolite composite membrane on separation of surfactant by ultra-filtration", J. Membrane Sci., 210, 209-225. https://doi.org/10.1016/S0376-7388(02)00324-1
  21. Saffaj, N., Persin, M., Younsi, S.A., Albizane, A., Cretin, M. and Larbot, A. (2006), "Elaboration and characterization of micro-filtration and ultra-filtration membranes deposited on raw support prepared from natural Moroccan clay: Application to filtration of solution containing dyes and salts", Appl. Clay Sci., 31, 110-119. https://doi.org/10.1016/j.clay.2005.07.002
  22. Saffaj, N., Younssi, S.A., Albizane, A., Messouadi, A., Bouhria, M., Persin, M., Cretin, M. and Larbot, A. (2004), "Preparation and characterization of ultra-filtration membranes for toxic removal from wastewater", Desalination, 168, 259-263. https://doi.org/10.1016/j.desal.2004.07.006
  23. Sichuan Yinfeng Chemical Co., Ltd. (2009), http://www.scyfchem.com/product4_e.htm.
  24. Tennison, S. (2000), "Current hurdles in the commercial development of inorganic membrane reactors", Membrane Tech., 2000(128), 4-9.
  25. U.S. Geological Survey (2006), Kyanite and Related Materials Minerals Handbook, 41.3.
  26. Wang, M.C., Wu, N.C. and Hon, M.H. (1994), "Preparation of nepheline glass-ceramics dental porcelain", Mater. Chem. Phys., 37, 370-375. https://doi.org/10.1016/0254-0584(94)90177-5
  27. Wang, Y.H., Tian, T.F., Liu, X.Q. and Meng, G.Y. (2006), "Titania membrane preparation with chemical stability for very hash environments applications", J. Membrane Sci., 280, 261-269. https://doi.org/10.1016/j.memsci.2006.01.027
  28. Workneh, S. and Shukla, A. (2008), "Synthesis of sodalite octahydrate zeolite-clay composite membrane and its use in separation of SDS", J. Membrane Sci., 309, 189-195. https://doi.org/10.1016/j.memsci.2007.10.033
  29. Yoshino, Y., Suzuki, T., Nair, B.N., Taguchi, H. and Itoh, N. (2005), "Development of tubular substrates, silica based membranes and membrane modules for hydrogen separation at high temperature", J. Membrane Sci., 267, 8-17. https://doi.org/10.1016/j.memsci.2005.05.020

피인용 문헌

  1. Oil Removal from Produced Water by Ultrafiltration using Polysulfone Membrane vol.34, pp.2, 2017, https://doi.org/10.1590/0104-6632.20170342s20150500
  2. Polyethersulfone (PES) ultrafiltration (UF) membranes loaded with silver nitrate for bacteria removal vol.2, pp.1, 2011, https://doi.org/10.12989/mwt.2011.2.1.025
  3. Separation of Water-Oil Emulsions Using Composite Membranes with a Cellulose Acetate Surface Layer vol.55, pp.7, 2010, https://doi.org/10.1007/s10556-019-00674-x