Abstract
In the many kind of construct-material, the concrete which has the high-strength and a durability is sufficient to use with structure-material. but the color of concrete is very monotony, so generally concrete isn't used the out surface. although color concrete is a method of expressing surface, the combination of pigment and cement cause many physical problem such as efflorescence phenomenon, strength degradation and so on. In this study, It attempt to develop the black mortar using the industrial granulated blast furnace slag and to evaluate basic physical properties compare with general color concrete to solve the color concrete problem. The result of experiment showed that the flow dropped mixing of pigment. but flow increased in proportion to the mixing rate in occasion of mortar that mix granulated blast furnace sla and black mortar which was made granulated blast furnace slag has more visible black color than any mortar.
본 연구는 생산원가 절감은 물론 에너지절감 및 환경보존을 목적으로 산업부산물인 고로슬래그 미분말을 컬러콘크리트의 활용방안으로 모색하고자 색상발현에 어려움이 있는 블랙색상을 선택하여 고로슬래그 미분말의 혼입률에 따른 기초 물성 및 색상발현정도 등을 확인하였다. 산업부산물인 고로슬래그 미분말을 활용한 컬러모르타르는 안료의 혼입시 유동성이 떨어지는 경향을 나타내었으나 입자표면이 산성피막에 의해 치밀하고 매끈하며 잠재수경성의 특성을 가진 고로슬래그 미분말의 혼업률에 비례하여 유동성이 증가하였다. 또한 일반 백색시멘트를 활용한 컬러모르타르보다 초기강도는 낮았으나 혼입시 우수한 장기강도 발현성을 나타내었다. 특히 현재 컬러콘크리트 시공시 색상발현에 가장 적합한 백색시멘트와 비교하여 동동하거나 그 이상의 색상발현성을 나타내었으며 명도 값 -30이하의 우수한 검정색상 발현이 가능하였다.