Abstract
Researches on resources recycling in the field of construction have made an extensive progress such as recycled aggregate of waste concrete and recycling of asphalt. On the other hand, there are almost never researches on pavement method with used waste frying oil. In South Korea, 0.2 million ton used waste frying oil is discharged every year. It is guessed that about 0.1 million ton used waste frying oil can be collected. If used waste frying oil is recycled, it is expected that disuse cost will be reduced and water pollution of rivers will be prevented. Therefore, the purpose of the study was to evaluate on mechanical features (strength, water resistance, chemical resistance, abrasion resistance, freezing and thawing resistance and permeable coefficient) whether dense graded permeable concrete mixing silica sand with flexible alkyd resin manufactured by making ester reaction with collected used waste frying oil to make alkyd resin could be applied to road pavement for non-roadway. The results of the study were as follows. In flexural strength, it had 1.6 times as much as road design standard 4.5MPa. In water resistance, chemistry resistance and freezing and thawing resistance, they had lack of strength in early age. As age went by, they didn't have large changes. And curing temperature had phenomenon of increase in strength at rather low temperature than high temperature by glass transition temperature of resin. Therefore, considering workability, strength and durability when it was applied to road pavement, it was reasonable that the mixing ratio of flexible alkyd resin was 10~15% in comparison with silica sand weight.
건설 분야의 자원재활용 연구는 폐콘크리트의 순환골재화, 아스팔트의 재활용 등에 광범위하게 진행되어온 반면에, 폐식용유를 원료로 한 도로용 포장공법에 관한 연구는 전무한 설정이다. 한국에서는 년간 20만톤의 폐식용유가 배출되며 이중 약 10만톤이 회수 가능한 것으로 추산된다. 폐식용유를 재활용한다면, 폐기비용을 절감할 수 있음은 물론, 하천의 수질오염도 방지할 수 있을 것으로 기대된다. 따라서 본 연구에서는 폐식용유를 회수하여 알키드 수지를 만들기 위해 에스테르반응을 시켜 제조된 유변성 알키드 수지에 규사를 혼입한 밀입도 투수콘크리트가 비차도용 도로 포장에 적용가능한지에 대한 역학적 특성(강도, 내수성, 화학저항성, 마모저항성, 동결융해저항성, 투수계수)을 평가하였다 실험결과 휨강도는 도로설계기준 4.5MPa에 1.6배의 결과를 보였으며, 내수성 및 화학저항성, 동결융해저항성은 재령 초기에 강도저하현상이 나타났으나, 재령이 증가함에 따라 큰 변화는 보이지 않았다. 그리고 양생온도는 수지의 유리전이온도 특성에 의해 고온에 비해 저온에서 강도증진현상을 보이는 것으로 나타났다. 따라서 도로포장용으로 적용시에는 작업성, 강도 및 내구성 측면을 고려해서 유변성 알키드 수지의 혼입률이 규사 중량대비 10~12%가 적정한 것으로 나타났다