Abstract
This work has been measured and analyzed the device degradation of NBTI (Negative Bias Temperature Instability) stress induced the increase of gate-induced-drain-leakage(GIDL) current for p-MOS transistors of gate channel length 0.13 [${\mu}m$]. From the relation between the variation of threshold voltage and subthreshold slop by NBTI stress, it has been found that the dominant mechanism for device degradation is the interface state generation. From the GIDL measurement results, we confined that the EHP generation in interface state due to NBTI stress led to the increase of GIDL current. As a results, one should take care of the increased GIDL current after NBTI stress in the ultra-thin gate oxide device. Also, the simultaneous consideration of reliability characteristics and dc device performance is highly necessary in the stress parameters of nanoscale CMOS communication circuit design.
본 논문은 게이트 채널 길이 0.13 [${\mu}m$]의 p-MOS 트랜지스터에서 음 바이어스 온도 불안정(NBTI) 전류 스트레스 인가에 의한 게이트유기 드레인 누설(GIDL) 전류를 측정 분석하였다. NBTI 스트레스에 의한 문턱전압의 변화와 문턱전압아래 기울기와 드레인 전류 사이에 상관관계로부터, 소자의 특성 변화의 결과로 열화에 대한 중요한 메카니즘이 계면 상태의 생성과 관련이 있다는 것을 분석하였다. GIDL 전류의 측정 결과로부터, NBTI 스트레스에 기인한 계면상태에서 전자-정공 쌍의 생성이 GIDL 전류의 증가의 결과를 도출하였다. 이런 결과로 부터, 초박막 게이트 산화막 소자에서 NBTI 스트레스 후에 증가된 GIDL 전류를 고려해야만 한다. 또한, 동시에 신뢰성 특성과 직류 소자 성능의 고려가 나노 크기의 CMOS 통신회로 설계의 스트레스 파라미터들에서 반드시 있어야 한다.