Abstract
This study conducted a static tensile test in order to prevent the lowering of load carrying capacity caused by critical sections made by over bolt holes in the base plate and the cover plate of steel member joints using high-tension bolts. The change of the load carrying capacity of joints was examined by comparison of the maximum load on joint fracture obtained from the tensile test with critical section rate and design strength. According to the results, the rate of decrease in strength was higher when the critical section rate was high, and in particular, decrease in strength was affected much more by critical sections in the base plate than by those in the cover plate. In high-tension bolt joints using over bolt holes for the base plate and the cover plate, load carrying performance was somewhat lower than that in joints using standard bolt holes, but the maximum tensile strength on facture was over 15% higher than design fracture strength. According to the results of this study, the use of over bolt holes in high-tension bolt joints had an insignificant effect on the lowering of load carrying capacity, so the allowance of over bolt holes in the joints of steel members is expected to enhance to the economy and efficiency of the works.
고장력볼트를 이용한 강부재의 체결에서 모재 및 덮개판의 과대공으로 인한 단면결손이 체결부에서 내하력의 저하가 우려되어 정적 인장시험을 실시하였다. 인장시험을 통하여 구해진 체결부의 파단시 최대하중을 단면결손율 및 설계강도와 비교하여 체결부의 내하력 변화를 파악하였다. 이에 따르면 단면결손율이 클수록 강도저하율이 컸으며 특히, 모재의 단면결손이 덮개판의 단면결손보다 강도저하에 대한 영향이 훨씬 큰 것으로 나타났다. 모재 및 덮개판을 과대공으로 제작한 고장력볼트 체결부는 표준공의 경우보다 내하성능이 다소 저하되었지만 파단시의 최대인장강도는 설계파단강도보다 15%이상 크게 나타났다. 본 연구에서는 과대공으로 제작된 고장력볼트 체결부에서 내하력저하에 미치는 영향이 미미하므로 강부재의 체결시공에 있어 과대공의 허용은 경제성과 효율성의 고취에 기여할 수 있을 것으로 판단되었다.