석고 및 미분시멘트에 의한 고로슬래그 미분말 치환 시멘트 모르타르의 초기강도 향상에 관한 기초적 연구
A Fundamental Study on Early Compressive Strength Improvement of the Blast Furnace Slag Cement Mortar Using the Fine Particle Cement and Gypsum
-
Han, Cheon-Goo
(Division of Architectural Engineering, Cheongju University) ;
- No, Dong-Hyun (Division of Architectural Engineering, Cheongju University)
- 투고 : 2009.10.07
- 심사 : 2009.10.15
- 발행 : 2009.10.30
초록
본 연구에서는 고로슬래그 미분말(이하 BS)사용 모르타르의 초기강도가 저하하는 문제점을 해결하고자 BS 20%치환 시멘트 모르타르에 자극제로 석고(이하 CS)와 고분말도의 미분시멘트(이하 FC)를 치환 사용한 경우의 기초적 물성을 검토한 것으로, 그 결과를 요약하면 다음과 같다. 먼저, 굳지않은 모르타르의 특성으로 유동성은 BS 치환율이 증가할수록 감소하였고, BS 20%에 CS를 치환한 경우는 치환율에 관계없이 큰 영향을 미치지 않은 것으로 나타났으며, FC를 치환한 경우는 치환율이 증가할수록 감소하는 것으로 나타났다. 압축강도는 BS 치환율이 증가할수록 초기재령에서 강도가 저하하는 것으로 나타났고, 재령 28일에서는 잠재수경성 반응에 기인하여 약간 증가하는 것으로 나타났다. BS 20 % 치환 모르타르의 초기 압축 및 휨 강도향상에 대하여 CS를 치환한 경우는 치환율이 증가함에 따라 초기재령에서 미소하게 증가하는 것으로 나타났고, FC를 치환한 경우는 치환율이 증가할수록 초기 및 28일 재령에서 강도가 크게 증가하는 것으로 나타났다. 종합적으로 BS 20% 치환 모르타르의 초기 강도 저하 문제의 해결로서 CS의 치환은 효과가 적고, FC 25%를 치환하여 사용하게 되면 OPC만을 사용한 Plain과 유사한 것으로 나타나 양호한 품질의 향상을 기대할 수 있을 것으로 분석된다.
The purpose of the study was to examine basic property at the time of applying cast ('CS' below) and high fineness fine particle cement ('FC' below) as a stimulant to 20% substitution cement mortar of ground granulated blast-furnace slag ('BS' below) to settle a problem that early strength of BS mortar is lowered. The results were as follows. First of all, as a characteristic of fresh mortar, liquidity was reduced as much as BS substitution rate was increased. When substituting CS for BS 20%, it didn't have a large effect regardless of substitution rate. When substituting FC, it was reduced as much as substitution was increased. In the event of compressive strength, it was reduced as much as BS substitution was increased in early age. In age 28, it was somewhat increased by reflection of potential hydraulicity. With regard to improvement of early compressive/bending strength of BS 20% substitution mortar, when substituting CS, in early age, they were a little increased as much as addition rate was increased. When substituting FC, in early and 28 age, they were largely increased as much as substitution rate was increased. To settle a problem that early strength of BS 20% substitution mortar was lowered, CS substitution has a little effect and FC 25% substitution was similar to plain with only OPC. Therefore, when substituting FC 25%, it is expected that its quality will be improved.