Abstract
In this research, experiments were conducted to find out whether polycarboxylate could be used as a crude steel admixture for practical work, depending on the change in the replacement level of the compound mixed into polycarboxylate. Its fluidity was satisfactory, its airspace was a bit smaller than the KS standard, and its unit volume weight was proven to meet the standard. The amount of bleeding was smallest in B2, and in terms of the solidification time, the first and the last solidification was faster in A1, B1, and C1. With regard to the compressive strength in early days as acharacteristic of hardened concrete, all addition rates of 7-day C2 displayed the highest strength value, among which the addition rate of 1.3% had the biggest strength performance tendency. The seal strength also showed the strength performance rate which was about one tenth as big as that of the compressive strength. The length change rate resulting from dryness and contraction was proven to be good, and once the appropriate AE air entraining agent is used, it is evaluated to be a very useful and practical compound out in the field.
본 연구에서는 폴리카본산계에 혼합 사용된 혼화제의 혼입율 변화에 따른 조강용 혼화제로서의 실무에서의 활용가능성 여부를 판단하고자한 실험연구 결과이다. 유동성은 만족하는 경향으로 나타났으며, 공기량은 KS규정보다 다소 작고 단위용적질량은 만족하는 것으로 나타났다. 블리딩 량은 B2가 가장 적게 나타났고, 응결시간은 A1, B1, C1에서 초결 및 종결이 빠르게 나타났다. 경화 콘크리트의 특성으로 조기재령의 압축강도 발형 경향은 7일 재령에서 C2의 모든 첨가율이 가장 높은 강도 값을 나타내었고 그 중 1.3%의 첨가율이 가장 큰 강도 발현경향을 나타내었다. 인장강도 역시 압축강도에 비해 약 1/10정도의 강도 발현율을 나타내고 있다. 건조 수축에 의한 길이 변화율은 양호한 편으로 나타났는데, 적당한 AE공기 연행제를 사용하면 실무에서 매우 유용한 혼화제로써의 사용이 가능할 것으로 판단된다.