This study was carried out to investigate whether adhesive used in manufacturing glulam can be used to bond wood and GFRP, when considering working process and economical efficiency. The six different glulams were manufactured, changing the adhesives and the mixing ratios of the adhesives, and investigated by the block shear test and the delamination of the water soaking or boiling water soaking. The three glulams were manufactured, using the resocinol resin based adhesive, the PVAc resin based adhesive and the epoxy resin adhesive, and the other three glulams, using the adhesives mixing resocinol resin and PVAc resin. The block shear strength is higher than $7.1N/mm^2$ in all types, which is standard of KS F3021. However, in the wood failure the block shear strength was the highest as 65.9% in the PVAc. The delamination of glulams glued with PVAc adhesive, which was 1.08% in water soaking and 4.16% in boiling water soaking, was lower than 5.00% which is the standard of KS F 3021, and the adhesive strength is good. In glulams glued with only resocinol resin adhesive, the wood layers were good as 1.26% in the water soaking delamination and 0.00% in the boiling water soaking delamination. The GFRP layers were not good as 21.85% in the water soaking delamination but were good as 1.45% in the boiling water soaking delamination.
본 연구에서는 작업성과 경제성을 고려하여 집성재 제작용 접착제를 목재와 유리섬유강화플라스틱(GFRP: Glass fiber reinforced plastic) 접착에 적용할 수 있는지를 검토하였다. 복합집성재는 접착제 종류와 혼합비에 따라 6가지 타입으로 제작하여 블록전단강도시험과 침지박리, 삶음박리 시험을 실시하였다. 레조시놀수지 접착제와 초산비닐 수지접착제, 에폭시수지 접착제를 사용한 복합집성재 3가지 타입과 레조시놀수지 접착제와 초산비닐수지 접착제를 혼합한 3가지 타입으로 총 6가지 타입으로 제작하였다. 블록전단시험 결과 모든 타입의 복합집성재가 KS F 3021 기준 $7.1N/mm^2$ 보다 높아 전단강도는 양호하였지만, 목파율에서는 초산비닐수지접착제가 65.9%로 가장 우수한 접착 성능을 나타내었다. 박리시험에서는 초산비닐수지 접착제를 사용한 경우 GFRP 접착층까지 포함된 경우 침지 박리는 1.08%, 삶음박리는 4.16%로 KS F 3021 합격기준인 5% 이하를 만족하였다. 레조시놀수지 접착제만을 사용 한 경우 목재 접착층은 침지박리 1.26%, 삶음박리 0%로 합격기준을 만족하였으나 GFRP 접착층을 포함시킬 경우 침지박리는 21.85%로 합격기준을 만족하지 못하였고 삶음박리의 경우만 1.45%로 만족하였다.