Abstract
To study an effective use of woods, three-ply hybrid laminated woods instead of crosslaminated woods which are composed of spruce in the face and three kinds of wood-based boards (MDF, PB, OSB) in the core were manufactured, and the effect of constitution elements for the core laminae on bending strength performances was investigated. Bending modulus of elasticity (MOE) of hybrid laminated woods had the highest values for the hybrid laminated wood types arranging OSB laminae in the core, and had the lowest values for those arranging MDF laminae in the core. These values were higher than those of various cross-laminated woods. The estimated bending MOEs of the hybrid laminated woods which were composed of perpendicular-direction lamina of spruce in the faces were similar to their measured values, regardless of wood-based boards in the core. However, those of the hybrid laminated woods which were composed of parallel-direction lamina of spruce in the faces had much higher values than those of their measured values, and it was necessary to revise the measured values. Bending modulus of rupture (MOR) of the hybird laminated woods had the highest value for those arranging OSB laminae in the core, and had the lowest values for those arranging PB laminae in the core unlike the bending MOE. By hybrid laminating, the anisotropy of bending strength performances was markedly decreased, and the differences of strength performances among wood-based boards were also considerably decreased.
이 연구에서는 목재의 효율적인 이용의 일환으로 스프루스 직교형적층재의 중층을 중밀도섬유판(medium density fiberboard, MDF), 파티클보드(particle board, PB) 및 배향성스트랜드보드(oriented strand board, OSB)의 3종류의 시판용 목질보드를 복합적층한 3층 목질계 복합적층재(패널)를 제작하여, 중층목질재료라미나의 구성엘리멘트가 복합적층재(패널)의 휨 강도성능에 미치는 영향을 조사하였다. 목질계 복합적층재의 휨 탄성계수는 중층에 배향성스트랜드보드(OSB)를 배열한 복합적층재에서 가장 높은 값을 나타내었고, 중밀도섬유판(MDF)을 중층에 배열한 복합적층재에서 가장 낮은 값을 나타내었다. 이 값은 중층에 섬유직각방향라미나를 배열한 다양한 종류의 직교형적층재 보다 높은 값을 나타내는 것이 확인되었다. 표층이 스프루스 섬유직각방향으로 된 복합적층재의 휨 탄성계수 예측치는 실측치와 비슷한 값을 나타내었으나, 표층이 스프루스 섬유방향으로 된 복합적층재의 휨 탄성계수 예측치는 실측치보다 높은 값을 나타내었다. 복합적층재의 휨 강도는 배향성스트랜드보드(OSB)를 중층에 배열한 타입에서 가장 높은 값을 나타내었고, 파티클보드(PB)를 중층에 배열한 타입에서 가장 낮은 값을 나타내어 휨 탄성계수와 약간 차이를 나타내었다. 복합적층에 의해, 복합적층재의 휨강도 성능의 이방성은 스프루스소재의 그것에 비해 현저히 감소하였고, 보드상호간의 강도성능의 차이도 현저히 감소하는 것이 확인되었다.