Abstract
The cation-exchange membrane which was sulfonated styrene-ethylene/buthlene-styrene(SEBS) block copolymer containing the high impact polystyrene (HIPS) was prepared via post-sulfonation and casting method using the epoxidized polybutadiene and divinylbenzene as crosslinking agents. Post-sulfonation was carried out with sulfuric acid as sulfonating agent and silver sulfate as initiator in the nitrogen atmosphere. The basic properties of membranes, degree of sulfonation (DS), water uptake, ion-exchange capacity (IEC), electrical resistance, and modulus have been examined. DS of membrane increased with increasing the sulfonation time. The maximum DS of membrane containing 10 wt% HIPS was 83.6 %. The water uptake and IEC of membranes gradually increased as increasing the DS. The maximum water uptake and IEC of membranes were 43.8 % and 1.14 meq/g, respectively. The lowest electrical resistance of membrane containing the 20 wt% HIPS was $83\;\Omega{\cdot}cm^2$. The electrical conductivity of membrane containing 10 wt% HIPS was $1.22\times10^{-4}S/cm$. The modulus of membrane increased with increasing DS and these values were 153 and $204\;kgf/cm^2$ before and after sulfonation, respectively.
본 연구에서 술폰화 SEBS/HIPS 양이온교환막을 epoxidized polybutadiene과 divinylbenzene 가교제로 가교시켜 캐스팅 및 술폰화방법으로 제조하였다. 막의 술폰화 반응은 황산과 silver sulfate를 사용하여 진행하였다. 또한, 막의 기본물성, 술폰화두 함수율, 이온교환용량, 전기저항 및 모듈러스를 확인하였다. 막의 술폰화도는 반응시간이 증가함에 따라 증가하였으며, 10 wt% HIPS가 혼합된 막의 술폰화도가 반응시간 120분에서 83.6%로 가장 높게 나타났다. 또한, 막의 함수율과 이온교환용량은 술폰화도가 증가함에 따라 증가하였으며 최대 43.8%, 1.14 meq/g이었다. 막의 전기저항은 20 wt% HIPS가 혼합된 양이온교환막이 $83\;\Omega{\cdot}cm^2$으로 가장 낮았으며 전기전도도는 10 wt% HIPS 혼합막이 $1.22\times10^{-4}S/cm$로 가장 우수하였다. 또한, 막의 기계적물성, 모듈러스는 술폰화도가 증가할수록 증가하였으며, 술폰화 전후 모듈러스값은 $153204\;kgf/cm^2$이었다.