Abstract
Z-type barium ferrite [($Ba_{3}Co_{0.8}Zn_{1.2}Fe_{24}O_{41}$, $Ba_{3+{\delta}}Co_{0.8}Zn_{1.2}Fe_{24}O_{41}$ ${\delta}$ = 3, 5, 7, 13 wt%. $Ba_{3}Co_{0.8}Zn_{1.2}Fe_{24+{\delta}}O_{41}$ ${\delta}$ = 5, 7, 10 wt% )] were synthesized using co-precipitation method. The microstructure and magnetic properties of synthesized particles were investigated. In all prepared particles M-type Ba ferrite is identified with Z-type Ba ferrite together. It is found that particles having 7 wt% for Ba and 5 wt% for Fe excess addition revealed high saturation magnetization, respectively. All synthesized particles showed relatively high coercivity for device application. This result may be attributed to the contribution of M-type Ba ferrite. Ba and Fe excess addition was not affected to the structural change of CoZnZ Ba ferrite. The certain amount of excess additions of Ba and Fe and the 2 step heat-treatment may be beneficial to the improvement of soft magnetic properties of Z-type barium hexa-ferrite
Z-Type 바리움 페라이트($Ba_{3}Co_{0.8}Zn_{1.2}Fe_{24}O_{41}$)를 공침법으로 제조하고 결정구조와 자기적 성질을 조사하였다. $Ba_{3+{\delta}}Co_{0.8}Zn_{1.2}Fe_{24}O_{41}$(${\delta}$ = 3, 5, 7, 13 wt%)와 $Ba_{3}Co_{0.8}Zn_{1.2}Fe_{{24}+{\delta}}O_{41}$(${\delta}$ = 5, 7, 10 wt%)의 조성을 가진 분말의 ${\delta}$ 값에 따른 자기적 성질의 변화를 조사하였다. 제조된 모든 바리움 페라이트에는 Z-type으로 상전이 하지 않은 M-type이 상당량 잔류하고 있었다. 포화자화는 Ba와 Fe의 과잉 첨가량 ${\delta}$가 각각 7 wt%와 5 wt% 일 때 최대로 나타났고 보자력은 조사된 모든 분말에서 다소 높게 나타났다. 높은 보자력은 M-type이 잔류하기 때문이다. 과잉의 Ba와 Fe 첨가에 따른 결정구조의 변화는 없었다. Z-type 바리움 페라이트의 연자성 특성을 향상시키기 위해서는 M-type이 Z-type 형성온도에서 상전이가 일어나도록 해야 함을 알았다.