Surface Characteristics of the Galvannealed Coating in Interstitial-Free High Strengthen Steels Containing Si and Mn

Si, Mn함유 IF 고강도 합금화 용융아연도금강판의 표면특성

  • Received : 2007.10.02
  • Published : 2008.02.10

Abstract

Surface-void defects observed on the galvannealed(GA) steel sheets in Interstitial-free high-strengthened steels containing Si and Mn have been investigated using the combination of the FIB(Focused Ion Beam) and FE-TEM(Field Emission-Transmission Electron Microscope) techniques. The scanning ion micrographs of cross-section microstructure of defects showed that these defects were identified as craters which were formed on the projecting part of the substrate surface. Also, those craters were formed on the Si or Mn-Si oxides film through the whole interface between galvannealed coating and steel substrate. Interface enrichments and oxidations of the active alloying elements such as Si and Mn during reduction annealing process for galvanizing were found to interrupt Zn and Fe interdiffusion during galvannealing process. During galvannealing, Zn and Fe interdiffusion is preferentially started on the clean substrate surface which have no oxide layer on. And then, during galvannealing, crater is developed with consumption of molten zinc on the oxide layer.

Keywords

References

  1. 1. K. Sato, K. Okuda and K. Sakata, 36th Mechanical Working and Steel Processing, p.201 (1994).
  2. I. Hertveldt, B. C. De Cooman and S. Classen, Metall. Mater. Trans. A, 31A, 1225 (1999).
  3. Y. Tobiyama and C. Kato, Tetsu-to-Hagane 89, 38(2003). https://doi.org/10.2355/tetsutohagane1955.89.1_38
  4. N. Fujibayashi, Y. Togawa and J. Sumiya, Cuc. Adv. Mater. Process. 10, 609 (1997).
  5. M. Isobe, C. Kato and K. Mochizuki, 39th MWSP Conf. Proc., ISS, p.15, p.121 (1998).
  6. P. Drillet, Z. Zermout, D. Bouleau, J. Mataigne and S. Claessens: Galvatech'04 Conf.Proc., p.1123 (2004)
  7. T. Kato, M. H. Hong, K. Nunome, K. Sasaki, K. Kurod andH. Saka, Thin Solid Film 319, 132 (1998). https://doi.org/10.1016/S0040-6090(97)01108-5