Abstract
Asphalt concrete pavements are susceptible to deformation and failure compared to cement concrete pavements. Epoxy is commonly used to enhance the bonding and durability of structures. Based on this concept, an epoxy and ceramics combined mixture was developed and applied to the field to estimate the pavement performance, Laboratory and field performance tests were conducted to observe the applicability of epoxy and ceramics composite materials compared to the conventional one. In this research, the epoxy and ceramics composite mixturewas used in two ways. 7 mm and 15 mm of thin surface layers using the mixture were constructed on cement and asphalt concrete pavements, respectively, after surface treatment. 12 months of field performance surveys were conducted to observe the resistances to the crack and deformation. According to the field performance tests, epoxy and ceramics combined mixture showed better bonding and field performances than the conventional one.
변형과 파손 등의 공용성능 문제가 발생하고 있는 아스팔트 포장과 콘크리트 포장에 비해 내구성능이 우수한 에폭시와 세라믹스를 결합한 혼합물을 도로포장에 적용하기 위하여 실내물성실험을 수행하고 현장에 적용하였다. 본 연구는 부착력과 내구성이 뛰어나 구조물 보수, 보강에 널리 사용되는 에폭시를 도로포장에 적용하기 위해서 세라믹스와 금속성분 등의 micro powder를 첨가하여 포장 재료로써의 공용성능을 확인하고 이를 현장에 적용하여 작업성과 시공성 등을 확인하였다. 콘크리트포장 현장의 시험시공은 파손된 기존 포장구간에 면처리 후 7 mm 박층으로 시공하였고, 아스팔트포장 현장의 시험시공은 파손된 기존 포장구간에 면처리 후 15 mm 박층으로 시공하여, 12개월 가량 균열 및 변형 발생여부를 관찰하였다. 에폭시와 세라믹스를 결합한 혼합물은 기존 포장과의 부착력이 뛰어났으며, 변형과 파손에 대한 저항성이 기존 포장재료에 비해 우수한 것으로 나타나 이를 도로현장에 적용할 경우, 공용성능 및 공용년한의 향상이 기대된다.