Abstract
It is well known that cracks in concrete decrease permeability and durability of concrete because cracks enhance the penetration of water or corrosive chemicals like as chlorides, carbon dioxides, sulfates and some others. But some of cracks in hardened cements may be sealed in case of contacting water. This phenomenon is called "self healing" and it has a close relation to hydration products newly formed on surfaces of cracks. Many studies on self healing in concretes commonly showed that CSH gel has been observed on crack surfaces. And some studies have reported that calcium hydroxides and ettringite were observed as well as CSH gel on crack surfaces. This study was carried out to investigate hydration products formed by self healing process and also examine the influence of waterproof admixture for concretes on self healing of cement. As a result of XRD, DSC, SEM and EDX analysis of crack surfaces, it was found that self healing of cement was related to CSH gel, calcium hydroxides and ettringite. And waterproof admixture increased fibrous (needle-like) hydration products which were in network form. It is estimated that such fibrous products are effective for self healing process of cement system.
콘크리트의 균열이 수밀성을 떨어트리고 내구성을 악화시키는 것은 이미 잘 알려진 사실이다. 균열에 의한 이러한 성능저하는, 콘크리트에 균열이 발생하면 물 뿐만이 아니라 염화물, 이산화탄소, 황산염과 같이 유해한 물질들의 침투가 용이해지기 때문이다. 하지만 균열이 물과 접촉하는 경우 일부는 폐쇄 된다. 이러한 현상을 self-healing이라고 하며, self-healing은 균열면에서 새로이 생성되는 수화물과 밀접한 관련이 있다. 콘크리트의 self-healing과 관련한 상당수의 연구에서 공통적으로 균열면 표면에서 CSH겔이 관찰됨을 확인하였다. 그러나 self-healing에 관한 일부 연구에서는 CSH겔 뿐만 아니라 수산화칼슘 및 에트링자이트가 균열 표면에서 관찰되었다고 보고하였다. 본 연구에서는 self-healing에 의한 수화생성물을 확인하고자 하였으며, 또한 구체방수재가 self-healing에 미치는 영향을 평가하고자 하였다. 균열 표면에 대하여 XRD, DSC, SEM, EDX 분석을 실시한 결과 시멘트계에서 self-healing은 CSH겔, 수산화칼슘, 에트링자이트와 연관이 있음을 확인하였다. 또한 구체방수재가 섬유상(또는 침상)의 수화물의 생성을 촉진하고 이들 수화물이 망목구조 형태를 이루는 것을 확인하였다. 이러한 섬유상의 수화물이 시멘트 계의 self-healing에 매우 효과적인 것으로 판단된다.