Abstract
The raw materials of permalloy were processed the ball-mill for 30 hours and the shape of permalloy particles was changed from sphere to flake type, which was observed using scanning electron microscope. The complex permittivity and permeability spectra and reflection loss of permalloy-rubber composite was measured using Network Analyzer in order to investigate the relationship between the microwave absorption and the material constants. The flake type permalloy-rubber composite showed high reflection loss, which was due to the high complex permittivity and permeability. Also, the matching frequency shifted toward lower frequency range with microwave absorber thickness, and the maximum reflection loss of -6.1 dB was observed in $1.65\;GHz{\sim}1.86\;GHz$ for a 1.3 mm thickness.
Permalloy를 30시간 볼밀 한 후 주사전자현미경으로 형상 및 입경을 분석하였으며, 볼밀 가공한 Permalloy의 입자들이 편편한 상을 가짐을 확인하였다. Permalloy를 실리콘 고무와 혼합하여 박형 전파흡수체를 제조하고 Network Analyzer을 이용하여 permalloy-고무 전파흡수체의 재료정수 및 전파흡수특성을 측정하였으며, 그들의 상관 관계를 비교 조사하였다. 가공한 permalloy-고무 복합재료는 높은 복소유전율 및 복소투자율을 가지며 미가공한 permalloy-고무 복합재료 보다 전파흡수 특성이 우수하였다. 또한 전파흡수체 두께에 따라서 정합주파수가 낮은 주파수 대역으로 shift 됨을 알 수 있고, 1.3 mm의 두께로 제조한 전파흡수체에서는 이동통신주파수 대역인 $1.65\;GHz{\sim}1.86\;GHz$에서 가장 우수한 전파흡수특성을 나타내었다.