Abstract
Polymer-modified mortars have been largely used as paving materials, flooring, waterproofing material, adhesives, anticorrosive linings, deck coverings, and other various materials. The various types and properties of the mixed polymer largely affect the characteristics of polymer-modified mortar that has been mixed with polymer latexes. Consequently, its application purposes are varied according to these properties. This paper investigates the typical properties of polymer-modified mortars that contain styrene and butyl acrylate latexes and styrene butadiene rubber. They are then tested to obtain air contents, water-cement ratios, flexural and compressive strengths, water absorption, and chloride-ion penetration. From the test results, the superior flexural strength of polymer-modified mortars is obtained at a S/BA-2 and a polymer-cement ratio of 20%. And, the water absorption and chloride ion penetration depth are greatly affected by the polymer-cement ratio rather than the types of polymer. In the polymer-modified mortar and concrete structures, aggregates are bound by such a co-matrix phase, resulting in the superior properties of polymer-modified mortar and concrete compared to conventional mortar and concrete.
폴리머를 혼입한 폴리머 시멘트 모르타르 및 콘크리트는 인장강도, 휨강도, 접착성, 수밀성, 내마모성 그리고 내약품성 등을 개선시키는데 우수한 효과가 있어 고성능이 요구되어지는 건축 구조물의 외장재, 바닥 마감재, 포장재, 방수재, 장식 코팅재, 그리고 보수재 등의 용도로 많이 사용되고 있다. 또한, 기존의 시멘트 콘크리트의 취약성을 보완하는 측면뿐만 아니라 보다 내구적이고 안정적인 구조재료의 역할을 할 수 있어 다양한 용도의 개발이 이루어지고 있다. 본 연구에서는 폴리머를 건축재료인 시멘트 콘크리트에 적용하기 위한 기초적 실험으로써 폴리머 시멘트 모르타르를 제작하여 그 특성을 파악하고 건축재료로서의 폴리머 이용 가능성을 확인하고자 하였다. 폴리머를 시멘트 모르타르에 혼입하여 적용해 본 결과, 보통 시멘트 모르타르에 비해 폴리머 시멘트 모르타르의 강도와 내구성 증진효과가 높게 나타나는 것을 알 수 있었다.