Synthesis of Polyurethane-polyacrylate Hybrid Emulsions

폴리우레탄-폴리아크릴레이트 하이브리드 에멀젼의 제조

  • Kang, Sang Yong (Department of Advanced Materials Engineering, College of Engineering Kongju National University) ;
  • Kim, Hyung Joong (Department of Advanced Materials Engineering, College of Engineering Kongju National University)
  • 강상용 (공주대학교 공과대학교 신소재공학부) ;
  • 김형중 (공주대학교 공과대학교 신소재공학부)
  • Received : 2008.01.11
  • Accepted : 2008.02.26
  • Published : 2008.03.31
Download PDF
⟨ Previous Next ⟩

Abstract

Hybrid emulsions consisting of polyurethane and acrylic polymer were prepared by emulsion polymerization of acrylic monomers and polyurethane water dispersions (PUD) as an emulsifier. At first, cationic type of PUD was synthesized with IPDI, PTMG1000, MDEA, and acetic acid. Then, acrylic monomers, such as MMA and n-BA, were copolymerized with the PUD without adding further surfactant. The tensile properties and water resistance increased with increasing acrylic monomer ratio. The hybrid emulsions showed better properties than the emulsions simply blended with the PUD and the acrylic emulsions.

이온성작용기를 갖는 수분산 폴리우레탄은 내수성이 약하기 때문에 수분에 노출된 환경에서의 사용이 제한된다. 폴리우레탄과 아크릴 고분자로 구성된 하이브리드 에멀젼을 수분산 폴리우레탄(PUD)을 emulsifier로 사용하고 아크릴 단량체들을 에멀젼 중합하여 제조하였다. 먼저 양이온성 PUD의 합성은 IPDI, PTMG1000, MDEA, AA가 사용되었고, 아크릴 단량체는 MMA와 n-BA를 사용하여 공중합하였다. PUD와 아크릴 단량체들의 중합비율에서 아크릴 단량체의 양이 증가할수록 내수성 및 인장강도가 좋아졌다. 결론적으로 단순 혼합된 에멀젼보다 하이브리드된 에멀젼이 더 우수한 물성을 나타내었다.