화학적 중합방법을 이용하여 HWNT/DAAQ를 합성하여 전기화학적 캐패시터용 전극 소재로서 전기화학적 특성을 연구하였다. XRD pattern 결과에서 MWNT/DAAQ의 표면에 DAAQ가 oligomer 상태로 존재하는 것을 확인 하였으며, SEM image를 통해 표면을 관찰하였고, TCA를 통해 열적안정성을 확인하였다. 활성탄과 MWNT/DAAQ에 기초한 전극의 용량은 1M의 $H_2SO_4$ 전해질 상에서 97F/g의 비방전용량을 확인되었으며, 또한 HWNT/DAAQ 복합 전극은 우수한 전기화학적 거동을 보이는 것을 관찰하였다.
MWNT/DAAQ(1,5-diaminoanthraquinone) composites were prepared by chemical polymerization of DAAQ onto MWNT and their capacitance was evaluated by means of cyclic voltammetry in 1M $H_2SO_4$ electrolyte. The performances of such cells have been compared with pure MWNT and DAAQ based electrodes. The SEM image shows that DAAQ was coated onto MWNT during polymerization and thermal stability from th TG analysis. The highest specific capacitance values of 97F/g were observed with AC-MWNT/DAAQ composite electrode. And MWNT/DAAQ based composite electrode also showed relatively good electrochemical behaviors better than MWNT electrode in sulfuric acid electrolyte.