The Effect of Surface Sealing on the Microleakage of Class V Composite Resin Restorations

제V급 복합레진 수복물의 표면전색이 미세변연누출에 미치는 효과

This in vitro study was performed to assess the effect of surface sealing on the microleakage of class V composite resin restorations that underwent several aging treatments. Class V cavities were prepared on the buccal surface of 100 sound extracted premolars and restored with a hybrid light-cured composite resin according to the manufacturer's instructions. They were randomly divided into two groups consisting of 50 samples: group I, without surface sealing, and group II, in which margins were etched and surface sealant was applied. After thermocycling, each group was divided into five subgroups, respectively, to represent the five aging treatments: group A = no further treatment (only thermocycling), B = toothbrushing, C = load cycling, D = toothbrushing followed by load cycling, and E = aging treatment in deionized water for six months. Microleakage was assessed by examining the penetration of 2% methylene blue dye. The following results were obtained: 1. At occlusal and cervical margins in groups without surface sealing, there was no significant difference in microleakage after the several aging treatments (p>0.05). 2. The occlusal margins of groups with surface sealing showed no significant differences after the several aging treatments (p>0.05). 3. In the cervical margins of groups with surface sealing, microleakage significantly increased after load cycling or aging in deionized water for six months (p<0.05). 4. The no-further-treatment group and the toothbrushing group with surface sealing showed less microleakage than the corresponding groups without surface sealing (p<0.05). 5. The surface-sealed groups with load cycling or aging in deionized water showed no significant difference in microleakage to the corresponding groups without surface sealing (p>0.05). In conclusion, the results of this study suggest that the surface sealant infiltrating through the gap of the cervical margin exerted a positive effect on microleakage at the initial stage, but the effect was not sufficient to overcome the stress generated by the cuspal flexure during occlusal loading and water absorption.

본 연구는 다양한 순환 및 시효 조건 하에서 제V급 복합레진 수복물의 표면전색이 미세변연누출에 미치는 효과에 대해 알아보고자 하였다. 100개의 건전한 소구치의 협면에 제V급 와동을 형성하고 제조사의 지시대로 광중합형 복합레진으로 수복하였다. 무작위로 나누어 표면전색을 시행하지 않는 I군과 표면을 산부식 후 표면전색을 시행한 II군으로 설정한 후 열순환(thermocycling)을 하였다. 각 군에서 하위군(A군= 열순환 외 다른 시효조건이 없는 군, B군=칫솔질군, C군=부하순환군, D군=칫솔질과 부하순환을 모두 시행한 군, E군=6개월간 증류수에 보관한 군)으로 나누어 각각에 맞는 시효조건을 시행하였다. 2% methylene blue 용액에 침윤시켜 변연의 미세누출정도를 평가하여 다음과 같은 결과를 얻었다. 1. 표면전색을 시행하지 않은 군의 교합변연과 치은변연에서 시효조건에 따른 미세누출의 유의한 차이는 보이지 않았다(p>0.05). 2. 표면전색을 시행한 군의 교합변연에서는 시효조건에 따른 미세누출의 유의한 차이가 없었다(p>0.05). 3. 표면전색을 시행한 군의 치은변연에서는 부하순환이나 6개월간 증류수에서 보관하는 시효과정을 거친 군에서 미세누출이 유의하게 크게 나타났다(p<0.05). 4. 시효조건이 없는 군과 칫솔질군의 경우, 표면전색을 시행한 군이 표면전색을 시행하지 않은 군에 비해 유의하게 적은 미세누출결과를 보였다(p<0.05). 5. 부하순환을 시행한 군과 6개월간 증류수에서 보관한 경우에는 표면전색을 시행한 군과 표면전색을 시행하지 않은 군 사이에 미세누출의 차이가 있었지만 유의차가 없었다(p>0.05). 따라서 이 연구의 결과는 변연부분의 미세간격으로 침투한 표면전색제가 처음에는 미세누출을 감소하는데 효과를 보여주었으나, 교합시 교두가 휘어져서 생기는 응력과 장기간의 수분흡수로 인한 변화를 견디기에 불충분함을 보여주었다.