Influence of the Solid Solution for Crystalline Phase on the Characterization of $Bi_2Sr_2Ca{_{n-1}}Cu_nO_x$(n=0,1,2) Thin Films

결정상에 대한 고용체가 $Bi_2Sr_2Ca{_{n-1}}Cu_nO_x$(n=0,1,2) 박막의 특성에 미치는 영향

  • Published : 2007.06.30
Download PDF
⟨ Previous Next ⟩

Abstract

[ $Bi_2Sr_2Ca{_{n-1}}Cu_nO_x$ ](n=0,1,2) thin fans have been fabricated by co-deposition at an ultra-low growth rate using ion beam sputtering(IBS) method. Bi 2212 phase appeared in the temperature range of 750 and $795^{\circ}C$ and single phase of Bi 2201 existed in the lower region than $785^{\circ}C$. Whereas, $PO_3$ dependance on structural formation was scarcely observed regardless of the pressure variation. And high quality of c-axis oriented Bi 2212 thin film with $T_c$(onset) of about 90 K and $T_c$(zero) of about 45 K is obtained. Only a small amount of CuO in some films was observed as impurity, and no impurity phase such as $CaCuO_2$ was observed in all of the obtained films.

이온 빔 스퍼터법을 이용하여 저속성장으로 동시 증착에 의해 $Bi_2Sr_2Ca{_{n-1}}Cu_nO_x$(n=0,1,2) 박막을 제작하였다. Bi 2212 상은 기판온도 $750{\sim}795^{\circ}C$의 범위에서 나타났으며, $750^{\circ}C$보다 저온 측에서는 Bi 2201의 단일상이 존재하였다. 그러나, 조성과 관계되는 $PO_3$은 압력 변화에 대해서는 관찰되지 않았다. 그리고 $45{\sim}90K$의 임계온도(Tc)를 갖는 c축 배향한 고품질의 Bi 2212 박막을 얻었다. 소수의 박막에서는 소량의 CuO가 불순물로 관찰되었으며, 얻어진 모든 박막에서 $CaCuO_2$ 의 불순물 상은 관찰되지 않았다.

Keywords

References

  1. 吉田 貞史, 蓴模(應用物理工學選書3, 棓風館), 1991
  2. 井上 泰宣 鐮田 善一郞, 獚畸 勝義, 蓴模物性入門(內田老鶴烳), 1994
  3. Y. Ikeda, H. Ito, S. Shimomura, Y. Oue, K. Inaba, Z. Hiroi and M. Takano, 'Phase and their Relations in the Bi-Sr-Cu-O System', Physica C(Netherlands), 159, 1-2, pp. 93-104, 1989 https://doi.org/10.1016/0921-4534(89)90099-3
  4. R. S. Roth, C. J. Rawn, B. P. Burton, and F. Beech, 'Phase Equilibria and Crystal Chemistry in Portions of the System SrO-CaO-$Bi_{2}O_{3}$-CuO, Part II-The System SrO-$Bi_{2}O_{3}$-CuO', J. Res. Natl. Inst. Stand. Technol. 95, 291, 1990 https://doi.org/10.6028/jres.095.029
  5. R. Muller, Th. Schweizer, P. Bohac, R. O. Suzuki and L. J. Gauckler, 'Compositional Range of the $Bi_{2}Sr_{2}CaCu_{2}O_{x}\;HT_{c}$-Superconductor and its Surrounding Phases', Physica C (Netherlands), Vol. 203, No. 3-4, pp. 299-314, 1992
  6. Y. Idemoto, S. Kobayashi and K. Fueki, 'Phase Diagrams and Ionic Defects in the 2212 and 2201 Phases of the Bismuth System', Physica C(Netherlands), Vol. 229, No. 1-2, pp. 47-58, 1994 https://doi.org/10.1016/0921-4534(94)90811-7
  7. L. Ranno, D. Martinez-Garcia, J. Perriere and P. Barboux, 'Phase Intergrowth in $Bi_{2}Sr_{2}Ca_{n-1}Cu_{n}O_{y}$ Thin Films', Phys. Rev. B, Vol. 48, No.18, pp. 13945-13948, 1993 https://doi.org/10.1103/PhysRevB.48.13945
  8. S. Hendricks and E. Teller, 'X-ray Interference in Partially Ordered Layer Lattices$\ddag$ ', J. Chem. phys. 10, 147, 1942 https://doi.org/10.1063/1.1723678
  9. Z. Z. Li, H. Rifi, A. Vaures, S. Megtert and H. Raffy, 'Synthesis of $Bi_{2}Sr_{2}CaCu_{2}O_{8}/Bi_{2}Sr_{2}CuO_{6}$ Superlattices with a $T_{c}$Enhancement Effect', Phys. Rev. Lett., 72, 25, pp.4033-4036, 1994 https://doi.org/10.1103/PhysRevLett.72.4033