Effect of heating rate on calcination heat treatment of YBCO thin films by DCA-MOD method

DCA-MOD 법으로 YBCO 박막 제조시 하소열처리의 승온속도 효과

High $J_c\;YBa_2Cu_3O_{7-x}$ superconducting films have been fabricated $LaAlO_3(100)$ substrate by MOD method using dichloroacetic acid(DCA) as chelating solvent for preparing precursor solution. Heating rate was varied in order to optimize the calcination heat treatment condition in DCA-MOD method. Coated films were calcined at lower temperature up to $500^{\circ}C$ in flowing humid oxygen atmosphere. The heating rate was calcined from $13.3^{\circ}C/min\;to\;0.28^{\circ}C/min$. Conversion heat treatment was performed $800^{\circ}C$ for 2 h in flowing Ar gas containing 1000 ppm oxygen with a humidity of 9.45%. Surface and cross sectional SEM microstructures showed that particle sizes were increased with heating rate at a calcination step. The amount of pores was increased with heating rate in the calcined films. Dense microstructure and sharp texture were developed in an YBCO films after conversion heat treatment. A high critical current density (Jc) of $1.26MA/cm^2$ (@77 K and self-field) was obtained for the YBCO film which was prepared with a heating rate of $0.28^{\circ}C/min$.