Abstract
In this study, we observed the shapes of CNTs formed with the thinckness of catalyst. Catalyst layer was grown by magnetron sputtering method and the thickness of Ni catalyst is the range from 20 to 80 nm. Also, the synthesis of CNT with Ni catalyst thickness was grown by hot-filament PECVD method. And, we investigated the composition of CNTs by using EDS measurement, also observed the shapes of CNTs by using HRTEM and FESEM measurements. In the result, through the TEM analysis, we observed the empty inside of CNTs and the multiwall CNTs, also confirmed the tip of CNT containing Ni. The composition of CNTs are consisted of an element of C, Ti, and Ni. As you shown the growth shapes of CNTs, the pretreatment of the catalyst before te growth of CNTs changed the particle size of the catalysts and grown the CNTs of the different shapes. Consequently, the best vertically alined and well-arranged CNTs exhibited from the substrate deposited at the catalyst thickness of 40 nm.
본 연구에서는 탄소나노튜브의 성장특성을 결정짓는 여러 요소 중 한가지인 촉매층 두께의 변화에 따라서 형성되어지는 탄소 나노튜브의 형태 변화를 관찰하였다. Ni 촉매층은 마그네트론 스퍼터링법을 이용하여 증착하였으며, Ni 촉매층의 두께는 $20{\sim}80\;nm$의 범위에서 설정하였다. 두께에 따른 Ni 촉매층 기판을 hot-filament 플라즈마 화학기상 증착(HF-PECVD) 장치를 이용하여 탄소나노튜브를 합성하였으며, 성장되어진 탄소나노튜브의 성분분석은 에너지 분산형 X-선 측정기(EDS)를 통해 분석하였고, 고배율 투과전자현미경(HRTEM) 분석과 전계방사 주사전자현미경(FESEM) 분석을 통해 성장된 탄소나노튜브 성장 형태를 관찰하였다. 그 결과로써, 고배율 투과전자현미경(TEM) 분석을 통해서는 탄소나노튜브는 내부가 비어있으며, 다중벽으로 구성되어 있는 것을 관찰하였고, 탄소나노튜브 상부에 니켈 금속이 포함된 것을 확인하였다. 이것은 분산형 X-선 측정을 통해 탄소나노튜브의 구성성분이 접착층인 Ti, 촉매층인 Ni 그리고 탄소(C)로 이루어졌음을 다시한번 확인하였으며. 성장형태에서도 알 수 있듯이 탄소나노튜브 성장 전에 행해여지는 전처리는 촉매층의 입자를 변화시키고 변화된 촉매층의 표면은 다른 형태의 탄소나노튜브를 성장시킴을 알 수 있었다. 결과적으로, 40 mn의 촉매층을 지니는 기판에서 가장 좋은 형태를 나타내는 탄소 탄소나노튜브가 성장되었음을 알 수 있다.