Adhesion Performance of Natural Rubber-based Pressure-Sensitive Adhesives for Protecting of Opto-functionalized Sheet

광기능성시트 보호용 천연고무계 점착제의 점착 물성

To prepare a natural rubber-based pressure-sensitive adhesive (PSA) for protection film of opto- functionalized sheet, natural rubber (NR) was blended with a DCPD type tackifier and three types of aliphatic hydrocarbon resins, respectively. Also, to supply low cohesion strength of NR, in the fixed ratio of tackifier, synthetic rubber, styrene-isoprene-styrene (SIS) block copolymer was blended with NR as a function of SIS contents. PSA performance of prepared PSAs was evaluated using probe tack and peel strength. Probe tack of NR/tackifier blends was increased with increasing tackifier contents, and showed maximum peak. In addition, probe tack of NR/tackifier blends slightly increased with increasing softening point of aliphatic hydrocarbon resins. Their peel strength increased up to 50 wt% of tackifier contents, but in the over contents of tackifier, they showed stick-slip failure mode. Finally, probe tack of NR/SIS/tackifier blends showed the maximum values at 20~40 wt% of tackifier contents, but at 20 wt% of tackifier contents, they showed fibrillation. For this reason, peel strength showed maximum values at 40 wt% of tackifier contents.

광기능성시트 보호용 점착제를 제조하기 위하여 천연고무와 DCPD계 점착부여수지, 세 종류의 지방족 점착부여수지를 이용하여 천연고무계 점착제를 제조하였다. 또한, 천연고무의 낮은 응집력을 대체하기 위하여 점착부여수지의 함량이 고정된 상태에서 SIS 블록공중합체를 함량비에 따라 첨가하여 점착제를 제조하였다. 제조한 점착제의 점착물성을 초기점착력과 박리강도로써 평가하였다. 천연고무/점착부여수지의 초기점착력은 점착부여수지의 함량이 증가함에 따라 증가하다 최대값을 보이고 감소하였다. 또한, 지방족계 점착부여수지의 연화점이 증가함에 따라 초기점착력이 다소 증가하였다. 점착부여수지의 함량이 50 wt%까지는 박리강도가 증가하였으나 그 이상의 함량에서는 혼합파괴 현상을 보였다. SIS가 블랜드된 점착제의 초기점착력은 지방족계 점착부여수지의 함량이 20~40 wt%에서 최대값을 보였으나 20 wt%에서 fibrillation 현상을 나타내었고 박리강도는 40 wt%에서 최대값을 나타내었다.