Hard Coatings on Polycarbonate Plate by Sol-Gel Reactions of (3-glycidoxypropyl)trimethoxysilane and Colloidal Silica

폴리카보네이트 판 위에 (3-glycidoxypropyl)trimethoxysilane과 Colloidal Silica의 졸-겔 반응을 이용한 하드 코팅

The hard coatings on the polycarbonate plate were performed with the object of substitution the glass in the car to the polycarbonate plate. In this research, (3-glycidoxypropyl)trimethoxysilane (GPTMS), colloidal silica (CS), and (3-aminopropyl)triethoxysilane (APS) were used to prepare the coatings by sol-gel process. The optimum conditions and formulation to get the excellent physical properties of the coating were determined. GPTMS and CS were hydrolyzed in ethanol, and then APS was added in this solution. Using these solution the hard coating were applied to the polycarbonate plate. The smooth coating which got the 2 H class in pencil hardness was formed. And this coating showed excellent abrasion resistant and adhesion property.

자동차의 유리를 폴리카보네이트로 대체하기 위하여 폴리카보네이트 판 위에 하드 코팅을 시도하였다. 본 연구에서는 (3-glycidoxypropyl)trimethoxysilane (GPTMS), colloidal silica (CS), (3-aminopropyl) triethoxysilane (APS)으로부터 졸-겔 과정을 이용하여 코팅을 형성하였는데, 이 때 가장 우수한 물성을 갖는 조건들을 찾아보았다. GPTMS와 CS를 에탄올 용매 안에서 가수분해 시킨 후에, APS를 첨가하여 코팅 액을 제조하고 이 코팅 액을 가지고 폴리카보네이트 판 위에 코팅을 실시하였다. 제조된 코팅 액으로부터 경도 2H의 투명하고 고른 면을 갖는 코팅 막을 형성할 수 있었으며, 형성된 코팅 막은 매우 우수한 내마모성과 접착력을 나타내었다.