Improvement of adhesion of Polyester Fabric and Knit by Corona Treatment

코로나 처리를 이용한 폴리에스테르 편·직물의 접착력 향상

Polyester fabrics and knits were corona treated with different current intensity (5, 10, 15, 20 A) and feeding speed (5, 10, 15 m/min). We confirmed the surface change of polyester fabrics and knits using scanning electron microscopy (SEM) and X-ray photoelectron spectrometer (XPS). And the change of physical properties through measuring the tensile strength, dry and wet bonding strength. Thermosetting reactive polyurethane hot melt adhesive was used in the adhesion of polyester fabrics and knits. Functional groups were introduced on PET fabrics and knits surface by treating the PET fabrics and knits in air atmosphere with corona discharge, and take placed unevenness, the result adhesion was improved. When consider both dry and wet bonding strength, we think that appropriate conditions in the PET fabrics corona treatment are feeding speed 10 m/min, current intensity 15 A and appropriate conditions in the mesh type PET knits corona treatment are feeding speed 10 m/min, current intensity above 10 A.

폴리에스테르 편 직물들을 전류세기 5, 10, 15, 20 A로, 공급속도 5, 10, 15 m/min로 코로나 처리하였다. 이들의 표면변화를 주사전자현미경(SEM)과 X-ray 광전자분석기(XPS)로 확인하였다. 또한 물리적 성질의 변화를 인장강도, 건조 시와 습윤 시의 접착강도를 통하여 측정하였다. 접착에 사용된 접착제는 열경화성 반응형 폴리우레탄 핫 멜트 접착제이다. 대기압에서 코로나 방전처리에 의해 폴리에스테르 편 직물에 관능기들이 도입되어졌고, 표면에 요철이 발생하여 그 결과 접착력은 향상되었다. 건조 시 및 습윤 시의 접착강도를 모두 고려할 때, PET 직물의 코로나 처리에 있어 적절한 조건은 공급 속도 10 m/min, 전류 세기 15 A라 생각되며, mesh형 PET knit는 공급 속도 10 m/min, 10 A 이상의 전류세기라 생각된다.