Abstract
The effects of binder and alumina content on the setting time, drying shrinkage, strength, freezing and thawing resistance and water absorption of polymer-modified pastes with alumina powder were examined. As a result the setting time of the polymer-modified pastes with alumina powder tended to delay with increasing binder content. Irrespective of the type of polymer, the drying shrinkage of the polymer-modified pastes with alumina powder tended to decrease with increasing binder content and alumina powder content. Regardless of the type of polymer, the tensile and adhesion strengths of the polymer-modified pastes with alumina powder tended to increase with increasing binder content and alumina powder content. Irrespective of the type of polymer, the durability factors of the polymer-modified pastes with alumina powder tended to increase with increasing alumina content. Irrespective of the type of polymer, the water absorptions of the polymer-modified pastes with alumina powder tended to decrease with increasing binder content and alumina content.
본 연구에서는 폴리머 개질 페이스트의 응결 시간, 건조수축, 강도, 동결융해저항성 및 흡수율에 미치는 결합재량 및 알루미나 분말 혼입량의 영향에 대하여 검토하였다. 그 결과, SBR 및 PAE폴리머 개질 페이스트의 응결 시간은 결합재량이 증가함에 따라 지연되는 경향을 보였다. 폴리머 종류에 관계없이 SBR PAE 폴리머 개질 페이스트의 건조수축은 결합재량 및 알루미나 분말 혼입량이 증가함에 따라 감소하는 경향을 나타내었다. 폴리머 종류에 관계없이 SBR 및 PAE 폴리머 개질 페이스트의 인장 및 부착강도는 결합재량 및 알루미나 분말 혼입량이 증가함에 따라 증가하는 경향을 나타냈다. SBR 및 PAE 폴리머 개질 페이스트의 내구성 지수는 폴리머 종류에 관계없이, 알루미나 분말 혼입량의 증가에 따라 증가하는 경향을 보였다. 폴리머 종류에 관계없이 SBR 및 PAE 폴리머 개질 페이스트의 흡수율은 결합재량 및 알루미나 분말 혼입량이 증가함에 따라 감소하는 경향을 나타내었다.