Abstract
Polyurethane (PU) was prepared with the compositions of polytetramethylene glycol (PTMG) having two different molecular weight (250, 1000 g/mol). The optimum composition of PTMG 250/1000 was 60/40 based on the mechanical properties. PU/organoclay nanocomposites were prepared with several kinds of organoclay. The mechanical properties of nanocomposite prepared with 93A were considerable. The improvement in tensile strength and modulus for PU/organoclay nanocomposite with the application of ultrasound compared to the PU/organoclay nanocomposite without the application of ultrasound was factors of 1.2, and hardness (shore A type) increased from 90 to 95. The difference in thermal degradation was not observed. The results of transmission electron micrographs and X-ray measurements suggest that the intercalated organoclay in PU matrix was observed.
분자량이 다른 polytetramethylene glycol (PTMG, 분자량: 250, 1000 g/mol)의 조성에 따라 polyurethane(PU)를 제조하였고 PTMG 250/1000의 비율이 60/40인 조성의 기계적 성질이 가장 우수하였다. 최적 조성의 PU에 다양한 종류의 organoclay를 첨가하여 PU/organoclay 나노복합체를 제조하였다. PU/organoclay 나노복합체의 인장강도와 신장율을 고려할 때 organoclay 93A가 가장 우수하였다. 초음파를 사용하여 organoclay를 분산시킨 나노복합체의 경우 초음파를 사용하지 않은 경우보다 인장강도 및 탄성율은 1.2배 증가하였고 경도는 90에서 95로 증가하였으며 신장율은 600% 이상 얻어졌다. 나노복합체의 열 안정성은 PU와 큰 차이를 보이지 않았다. X선 회절 (XRD, X-ray diffraction)을 통하여 나노복합체내에 있는 organoclay의 층간 판상거리가 2.5 nm에서 3.3 nm로 증가함을 관찰하였다. 이는 organoclay가 PU 내에서 완전 박리가 안되고 삽입된 것을 의미하며 TEM (transmission electron micrograph)에 의해 확인되었다.