Characteristics of Bi2212 Round-wire Depending on Heat Treatment Condition

열처리조건에 따른 Bi-2212 라운드형 선재의 특성

  • Published : 2006.09.01
Download PDF
⟨ Previous Next ⟩

Abstract

The characteristics of Bi2212 round wire was systematically studied depending on different heat treatment conditions. Initial wire was drawn after routine PIT (Powder In Tube) process. The wire was divided into 3 pieces with 10 cm in length and 2.5 mm in diameter. 3 wires were pre-heat treated separately by different heat treatment schedules, heated in air and nitrogen atmosphere and centrifugally melted. Pre-heated wires were annealed at $845^{\circ}C$ for 40 hours in oxygen atmosphere. SEM results indicate that all pre-heated wires showed highly oriented microstructure. However the wire by centrifugally melted process showed higher density and better electric properties as compared with 2 other wires pre-heated in air and nitrogen atmosphere. The critical current of a centrifugally melted wire was about 18 A in 77 K.

Keywords

References

  1. S. Nagaya, T. Nakano, H. Morita, M. Minami, H. Kawashima, T. Sato, 'Proposal of 40 MWh hybrid power storage System with Superconducting Flywheel and HTc-SMES'. Adv. Spercond. X. pp. 1301-1304. Vol.2. 1998
  2. T. Koizmumi, T. Nakatsu, N.Ohtani, Y. Aoki, T. Hasegawa, N. Hirano, S, Nagaya, 'Development of Large Current Capacity Bi-2212 Monolithic Conductors'. Physica C. pp. 1025-1029. Vol. 392-396, 2003 https://doi.org/10.1016/S0921-4534(03)01182-1
  3. M.D. Collings, R.M. Sumption, D.R. Scanlan, L.R. Dietderich, R.S. Motowidlo, Y. Sokolowski, T. Aoki. 'Bi: 2212/Ag-based Rutherford cables : production. processing and properties'. Supercond. Sci. Technol. pp. 87-96, 12(2), 1999 https://doi.org/10.1088/0953-2048/12/2/006
  4. K. Heine, J. Tenbrink, H. Krauth, 'Critical currents and flux pinning in Ag stabilized high Tc Superconductor wires'. Cryogenics, pp. 422-426, Volume 30, 1990 https://doi.org/10.1016/0011-2275(90)90169-D