초록
0.03Pb$(Sb_{0.5}Nb_{0.5})O_{3}-0.03Pb(Mn{1/3}Nb{2/3)O_{3}-(0.94-x)PbTiO_{3}-xPbZrO_{3}$ ceramics doped with $CeO_{2}$ were synthesized by conventional bulk ceramic processing technique. Phases analysis, microstructures and piezoelectric properties were investigated as a function of $CeO_{2}$ content (0.03, 0.05, 0.1 0.3, 0.5 and 0.7 wt%). Microstructures and phases information were characterized using a scanning electron microscope (SEM) and an X-ray diffractometer (XRD). Mechanical quality factor ($Q_{m}$) and coupling factor(kp) were obtained from the resonance measurement method. Both $Q_{m}$ and $k_{p}$ were shown to reach to the maximum at 0.1 wt% $CeO_{2}$. In order to evaluate the stability of resonance frequency and effective electromechanical coupling factor ($K_{eff}$) as a function of $CeO_{2}$, the variation of resonance and anti-resonance frequency were also measured using a high voltage frequency response analyzer under various alternating electric fields from 10 V/mm to 80 V/mm. It was shown that the stability of resonance frequency and effective electromechanical coupling factor were increased with increasing the $CeO_{2}$ contents.