Physico-Mechanical Properties and Formaldehyde Abatement of Particleboard Mixed with Gingko Tree Leaves

은행나무 잎을 혼합하여 제조한 파티클보드의 물리.기계적 성질과 포름알데히드 저감효과

This study was conducted to find potentialities of the leaves of gingko tree (Gingko biloba L.) which has been planted as a roadside tree in Korea because of its resistance on air pollution, insect, fungi, etc. Various amounts of the leaves were mixed with wasted wood particles to manufacture particleboard. Their influences on physical and mechanical properties and the formaldehyde emission of PB were investigated. Physical and mechanical properties, such as density, modulus of rupture (MOR), and internal bond (IB) strength, of manufactured particleboard were not much different from those of control board. Formaldehyde emission values were decreased with increasing amount of leaves in PB prepared. Especially, particleboard made with 3 percent of leaves was decreased to $1.66mg/{\ell}$ in formaldehyde emission, which is about 40% lower emission than that of control. From these results, the leaves of gingko tree may be considered as a formaldehyde emission lowering additive in a functional PB manufacturing process.

본 연구에서는 대기오염에 대한 저항성과 내충성, 항균성 등이 강하여 가로수로 많이 심어진 은행나무에 있어서, 그 잎의 파티클보드 제조 원료로서의 가능성을 모색하고자 하였다. 이를 위해 은행나무 잎을 분쇄한 다음 목재 파티클에 소량 혼합하여 파티클보드를 제조하였다. 은행나무 잎을 혼합하여 제조한 파티클보드의 물리, 기계적 성질을 조사하고 포름알데히드 방출량의 저감효과에 대해 검토하였다. 목재 파티클에 대하여 은행나무 잎을 $1{\sim}5%$ 첨가하여 제조한 파티클보드는 은행나무 잎을 첨가하지 않은 대조구에 비해 밀도, 함수율, 흡수두께팽창률 등 물리적 성질과 휨강도, 박리강도와 같은 기계적 성질은 크게 감소하지 않았으며 모두 KS 파티클보드의 기준을 만족하였다. 은행나무 잎의 혼합량에 따라 포름알데히드 방출량은 점차 감소하였으며, 특히 은행나무 잎이 3% 첨가된 파티클보드의 포름알데히드 방출량은 $2.81mg/{\ell}$에서 $1.66mg/{\ell}$로 대조구에 비해 약 40% 감소하였다. 은행나무 잎이 지닌 고유한 항균성에 덧붙여 본 연구로부터 얻어진 결과는 낙엽으로 폐기되는 은행나무 잎을 원료로 포름알데히드 방출량이 낮은 기능성 파티클보드를 제조할 수 있다는 새로운 사실을 보여주고 있다.