Abstract
Electrochemical hydrogenation/dehydrogenation properties were studied for a single particle of a Mm-based(Mm : misch metal) hydrogen storage alloy($MmNi_{3.55}Co_{0.75}Mn_{0.4}Al_{0.3}$) for the anode of Ni-MH batteries. A carbon fiber microelectrode was manipulated to make electrical contact with an alloy particle, and the cyclic voltammetry and the galvanostatic charge/discharge experiments were performed. A single particle of the alloy showed the discharge capacity of 280[mAh/g], the value being 90[%] of the theoretical capacity. Data were compared with that of the composite film consisting of the alloy particles and a polymer binder, which is more practical form for Ni-MH batteries. Additionally, pulverization of the alloy particles are directly observed. Compared with the conventional composite film electrodes, the single particle measurements using the microelectrode gave more detailed, true information about the hydrogen storage alloy.
본 논문은 마이크로 전극 측정 시스템을 사용하여 차세대 신동력 산업인 HEV(Hybrid Electric Vehicle) 및 수소연료전지(PEMFC) 차량용 니켈 수소전지의 전극소재로 사용되고 있는 수소저장합금(Mm : misch metal, $MmNi_{3.55}Co_{0.75}Mn_{0.4}Al_{0.3}$)의 단일 입자에 대해 전기화학적 수소 흡방출 특성 평가를 수행 하였다. 즉 Carbon fiber 마이크로 전극을 합금 입자 한개 위에 전기적인 접촉을 이루도록 조정하고, Cyclic Voltammetry 및 Galvanostatic 충방전 실험을 수행하였다. 그 결과 단일 입자의 방전용량은 약 280[mAh/g]로 이론용량의 약 90[%]의 특성을 보여 주었다. 데이터는. 실제 Ni-MH전지를 구성하는 합금입자 그리고 폴리머 바인더로 구성된 Composite film 전극과 비교 하였다. 추가적으로 합금의 단일 입자에 있어 in situ 미분화 현상을 관찰하였다. 마이크로 전극 측정 시스템에 의한 단일 입자의 전기화학적 평가는 기존의 Composite Film 전극에 비해 수소저장합금에 대해 보다 상세하고 정확한 정보를 쉽게 얻을 수 있었다.