Electrochemical Hydrogenation Behavior of Surface-Treated Mg-based Alloys for Hydrogen Storage of Fuel Cell

연료전지의 수소저장용 마그네슘계 합금의 표면제어에 의한 전기화학적 수소화 거동 연구

  • 김호성 (한국생산기술연구원, 광주연구센터, 광.에너지팀) ;
  • 이종호 (한국생산기술연구원) ;
  • 부성재 (한국생산기술연구원)
  • Published : 2006.08.31

Abstract

The effects of surface treatment on the hydrogen storage properties of a $Mg_2Ni$ alloy particle were investigated by the microvoltammetric technique, in which a carbon-filament microelectrode was manipulated to make electrical contact with the particle in a KOH aqueous solution. It was found that the hydrogen storage properties of $Mg_2Ni$ at room temperature were improved by the surface treatment with a nickel plating solution. The sodium salts(sodium phosphate and sodium dihydrogen citrate) contained in the nickel plating solution made the alloy form an amorphous-like state, resulting in an improved hydrogen charge/discharge capacity at room temperature as high as about 150[mAh/g] from the original value of 17[mAh/g]. Potential-step experiment was carried out to determine the apparent chemical diffusion coefficient of hydrogen atom($D_{app}$) in the alloy. Since the alloy particle we used here was a dense, conductive sphere, the spherical diffusion model was employed for data analysis. $D_{app}$ was found to vary the order between $10^{-8}{\sim}10^{-9}[cm^2/s]$ over the course of hydrogenation and dehydrogenation process.

[ $Mg_2Ni$ ]계 합금 입자의 수소저장 특성에 대한 표면처리 효과가 마이크로 전극 측정법에 의해 검토되었다. 카본-섬유로 된 마이크로 전극을 KOH 수용액 속에서 조정자를 사용하여 수소 단일입자에 접촉시켰다. 상온에서 $Mg_2Ni$ 합금의 수소저장 특성은 니켈 도금용액에 의한 표면 처리에 의해 크게 개선되었다. 니켈 도금용액 속에 있는 함유된 나트륨염(sodium phosphate 및 sodium dihydrogen citrate)이 합금을 아몰퍼스와 같은 형태로 만들었으며, 그 결과 상온에서 수소 흡장/방출 용량이 최초의 17[mAh/g]에서 150[mAh/g]로 향상되었다. 합금 입자 내에서 수소원자의 겉보기 화학적 확산계수를 계산하기 위하여 Potential-step 실험을 실시하였으며 데이터 해석을 위해 구형확산 모델을 적용하였다. 실험결과로서 겉보기 확산계수($D_{app}$)는 수소 흡장 및 방출되는 전 과정에서 $10^{-8}{\sim}10^{-9}[cm^2/s]$ 수준인 것으로 확인되었다.

Keywords

References

  1. N. Cui, B. Luan, H. K. Liu, H.J.Zhao, S. X. Dou, J. Power Sources, 55(1995)
  2. T. Kohno, S. Tsuruta, M. Kanda, The 37th Battery Symp., (1996) 390
  3. J. C. Bolcich, A. A. Yawuy, H. L. Corso, H. A. Pertti and C. O Anala, Int. J. Hydrogen Energy, 19(1994) 605-609 https://doi.org/10.1016/0360-3199(94)90219-4
  4. J. L. Luo, N. Cui, J. Alloys and Comp., 264(1998) 299-305 https://doi.org/10.1016/S0925-8388(97)00277-6
  5. W. Liu, H. Wu, Y. Lei, Q. Wang, J. Wu, J. Alloys and Comp., 261(1997) 289-294 https://doi.org/10.1016/S0925-8388(97)00220-X
  6. Y. Q. Lei, Y. M. Wu, Q. M. Yang, J. Wu and Q. D. Wang, Z. Phys. Chem., 183, (1994) 379 https://doi.org/10.1524/zpch.1994.183.Part_1_2.379
  7. C. Iwakura, H. Inoue, S. G. Zhang, S. Nohara, J. Alloys and Comp., 270(1998) 142-144 https://doi.org/10.1016/S0925-8388(98)00517-9
  8. H. Ura, T. Nishina, I. Uchida, J. Electroanal. Chem., 396, (1995) 169 https://doi.org/10.1016/0022-0728(95)03975-M
  9. K. Sapru, et al. ; US Pat. 4623597(1986)
  10. Y. Q. Lei, Y. M. Wu, Q. M. Yang, J. Wu and Q. D. Wang, Z. Phys. Chem., 183(1994) 379 https://doi.org/10.1524/zpch.1994.183.Part_1_2.379
  11. A. A. Nayeb-Hashemi and J. B Clark, Binary Alloy Phase Diagrams(1991) 2530
  12. J. Alloys and Compounds 415, (2006) 266-270 https://doi.org/10.1016/j.jallcom.2005.08.002
  13. J. Alloys and Compounds 356-357, (2006) 612-616 https://doi.org/10.1016/S0925-8388(02)01285-9
  14. K. Naito, T. Matsunami, K. Okuno, M. Matsuoka, C. Iwakura, J. Applied Electrochemistry, 24(1994) 808-813 https://doi.org/10.1007/BF00578099