Characterization of PET Thick & Thin Yarns on the Spinning Speed and Over Feed Ratio

방사속도 및 공급률에 따른 PET 태세사(Thick & Thin yarn)의 특성

  • Published : 2006.06.01
Download PDF
⟨ Previous Next ⟩

Abstract

The aim of this work is to develop Thick-Thin polyester yarn(T-T yarn) with finer than 1 denier mono filament. The manufacture of T-T yarns were carried out in a draw-winder using 85d/72f PET filament with various spinning speed of 2700, 2900, and 3100 m/min, respectively. The structure and physical properties of T-T yarns with spinning speed and over feed ratio were examined by draw-winder processing the sample in $100^{\circ}C$ water for 20 min and drying in 120, 140, 160, and $180^{\circ}C$ of dry air for 20 min. The crystallinity, the birefringence and the initial elasticity modulus of T-T yarns increased with increased spinning speed of filament and the heat treatment temperature but at the temperatures higher than $140^{\circ}C$ the increased rates show a tendency to decrease. Moreover, the initial modulus and the tenacity of T-T yarns increased with decreasing the over feed ratio of filament and the those of T-T yarns decreases with increasing the heat treatment temperature. The shrinkage of T-T yarns decreased with decreasing spinning speed and increased over feed ratio of filaments. Consequently, the results indicate that the best T-T yarn under 1 denier was optimized from PET filament with spinning speed of 2700 m/min and over feed ratio of 0.67

Keywords

References

  1. J. Friedrich, I. Loeschcke, H. Frommelt, H. Reiner, H. Zimmermann, and P. Lutgen, Ageing and Degragation of Poly(ethylene terephthalate) in an Oxygen Plasma, Polym. Degrad. Stability, 31, 97-114(1991) https://doi.org/10.1016/0141-3910(91)90099-D
  2. B. I. Kim, T. K. Kim, and Y. J. Lim, The Porosity and the Dyeability of Polyester Fiber Treated with Sodium Hydroxide Aqueous Solution, J. Korean Soc. Dyers & Finishers, 12, 44-52(2000)
  3. S. Y. Lee, S. W. Park, and S. S. Kim, A Study on the High Functional Finishing of Polyester Flat Fabrics Treated with Chitosan, J. Korean Soc. Dyers & Finishers, 16, 22-30(2004)
  4. M. S. J oung, D. S. J oung, K. H. Kim, and M. C. Lee, Heat Setting and Dyeing Properties of PET Ultrarnicrofiber, J. Korean, Fiber, Soc., 36, 696-703(1999)
  5. M. S. Park and J. H. Yoon, The Change of Crystal Structure and Physical Properties of Partially Oriented Polyester Yarn(POY) on the Draw Ratio and Heat Setting Temperature, J. Korean Soc. Dyers & Finishers, 12, 25-32(2000)
  6. H. Y. Chol and J. S. Lee, Surface Modification of PET Irradiated by Ultra-Violet(Part I), Transformation of Chemical Structure and Surface Properties, J. Korean Soc. Clothing & Textiles, 29, 561-568(2005)
  7. J. H. Jang, S. I. Eom, and Y. H. Kim, Continuous Surface Modification of PET Film via UV Irradiation, Effect of Spectral Irradiance, J. Korean, Fiber, Soc., 39, 100-107 (2002)
  8. K. Koo, S. S. Kim, Y. M. Park, J. Y. Yu, B S. Koo, and S. C. Yoo, Physicochemical Characterization of PET Fabrics Treated with Chitosan after Exposure to $O_{2}$ Low Temperature Plasma, Especially by KES evaluation, J. Korean Soc. Dyers & Finishers, 17, 26-36(2005)
  9. S. W. Woo and C. G. Cho, Hydrophilic Modification of PET by Using Block Copolymer, Molecular Structure and Hydrophilicity of PET-PEG Black Copolymers, J. Korean, Fiber, Soc., 36, 211-218(1999)
  10. C. G. Cho, S. W. Woo, K. L. Choi, and S. S. Hwang, Improvement of Antistatic Performance of PET by Using Block Copolymer, Influence of Molecular Weight of Poly(ethylene glycol) on the Thermal Properties and Moisture Absorptivity of PET-PEG Multi-Block Copolymer, J. Korean, Fiber, Soc., 21, 821-829(1997)
  11. M. S. Park, The Crystal Structure and Mechanical Properties of Thick & Thin Yam According to Production Condition, J. Korean Soc. Dyers & Finishers, 17, 43-48(2005)