PVA/PSSA-MA막을 이용한 수증기 투과 성능에 관한 연구

Performance Investigation of Water Vapor Permeation Using PVA/PSSA-MA Membranes

  • 임지원 (한남대학교 공과대학 화학공학과) ;
  • 윤태일 (한남대학교 공과대학 화학공학과) ;
  • 서무영 (한남대학교 공과대학 화학공학과) ;
  • 조현일 (한남대학교 공과대학 화학공학과) ;
  • 하성룡 ((주)에어레인) ;
  • 남상용 (경상대학교 고분자공학과)
  • Rhim Ji-Won (Department of Chemical Engineering, Hannam University) ;
  • Yun Tae-Il (Department of Chemical Engineering, Hannam University) ;
  • Seo Moo-Young (Department of Chemical Engineering, Hannam University) ;
  • Cho Hyun-Il (Department of Chemical Engineering, Hannam University) ;
  • Ha Seong-Yong (AIRRANE Co., Ltd.) ;
  • Nam Sang-Yong (Department of Polymer Science and Engineering, Engineering Research Institute, Gyeongsang National University)
  • 발행 : 2006.06.01

초록

Poly(vinyl alcohol) (PVA)와 가교제 Poly(styrene sulfonic acid-co-maleic acid) (PSSA-MA)을 적용하여 제조된 막을 이용하여 수증기 및 공기에 대한 막 투과 실험을 하였다. 또한 PVA/PSSA-MA막에 대한 PSSA-MA의 함량별로 접촉각을 측정하였으며 함량이 3 wt%에서 접촉각이 가장 낮았고 함량이 증가할수록 접촉각은 증가하였다. $35^{\circ}C$에서 PSSA-MA 함량 변화에 따른 수증기 투과도는 7 wt%에서 15300 Barrer (1 Barrer=$10^{-10}cm^3(STP){\cdot}cm/cm^2{\cdot}s{\cdot}cmHg$)로서 최대를 나타내었다. 그리고 $25^{\circ}C$에서 PVA/PSSA-MA막의 수증기 투과 성능은 $35^{\circ}C$와 유사한 경향을 보였다. 공기의 투과도는 PSSA-MA의 함량이 7 wt%에서 최대가 되었으며 $35^{\circ}C$C에서 146 Barrer를 나타내었고, $P(H_2O)/P(Air)$$25^{\circ}C$에서 109.2로 최대를 나타내었다.

The crosslinked poly(vinyl alcohol) (PVA) mwmbranes with poly(styrene sulfonic acid-co-maleic acid) (PSSA-MA) were used to measure the water vapor and air permeabilities at 25 and $35^{\circ}C$. In addition, the contact angles of crosslinked PVA membranes were observed and increased with PSSA-MA contents. The water vapor permeability of 15300 Baller (1 Baller=$10^{-10}cm^3(STP){\cdot}cm/cm^2{\cdot}s{\cdot}cmHg$) was shown the maximum value at $35^{\circ}C$ when PSSA-MA=7 wt% membrane was used. The gas permeability of 146 Barrer was indicated the maximum at PSSA-MA=7 wt% at $35^{\circ}C$ and $P(H_2O)/P(Air)$ was the highest value 109.2 at $25^{\circ}C$.

키워드

참고문헌

  1. L. Z. Zhang and Y. Jiang, 'Heat and mass transfer in a membrane-based energy recovery ventilator' J. Membr. Sci. 163 29-38 (1999) https://doi.org/10.1016/S0376-7388(99)00150-7
  2. G. W. Brundrett, 'Handbook of Dehumidification Technology', ButterWorths, London (1987)
  3. U. Sander and H. Janssen, 'Industrial application of vapour permeation', J. Membr. Sci., 61, 133-129 (1991)
  4. S. Y. Nam, Y. J. Kim, S. W. Cheon, and J. W. Rhim, 'Removal of VOCs from water by vapor permaetion through PU/PDMS membrane', Membrane J., 14(2), 157 (2004)
  5. Moon-Sung Kang, Young-Jin Choi and Seung-Hyeon Moon, 'Water-swollen cation-exchange membranes prepared using poly(vinyl alcohol) (PVA)/poly(styrene sulfonic acid-co-maleic acid) (PSSAMA)' J. Memb. Sci., 207 Issue 2, 157-170 (2002) https://doi.org/10.1016/S0376-7388(02)00172-2
  6. 염충균, 이정민, 홍영택, 김성철, '연속흐름방식에 의한 기체투과특성 측정 및 분석' Membrane J., 9(3), 141-150 (1999)
  7. Takasgi Nishino, Masashi Meguro, and Katsuhiko Nkamae, 'poly(vinyl alcohol) with low surface free energy by fluorination', International Journal of Adhesion & Adhesives, 19, 399-403 (1999) https://doi.org/10.1016/S0143-7496(98)00063-3