Fatigue Strength Depending on Position of Cracks for Weldments

  • Lee Hae-Woo (Welding Research Team, Hanjin Heavy Industries) ;
  • Park Won-Jo (School of Mechanical and Aerospace Engineering, Gyeongsang National University, Institute of Marine Industry)
  • 발행 : 2006.05.01
PDF 다운로드
⟨ 이전 논문 다음 논문 ⟩

초록

This is a study of fatigue strength of weld deposits with transverse cracks in plate up to 50 mm thick. It is concerned with the fatigue properties of welds already with transverse cracks. A previous study of transverse crack occurrence, location and microstructure in accordance with welding conditions was published in the Welding Journal (Lee et al., 1998). A fatigue crack develops as a result of stress concentration and extends with each load cycle until fatigue occurs, or until the cyclic loads are transferred to redundant members. The fatigue performance of a member is more dependent on the localized state of stress than the static strength of the base metal or the weld metal. Fatigue specimens were machined to have transverse cracks located on the surface and inside the specimen. Evaluation of fatigue strength depending on location of transverse cracks was then performed. When transverse cracks were propagated in a quarter-or half-circle shape, the specimen broke at low cycle in the presence of a surface crack. However, when the crack was inside the specimen, it propagated in a circular or elliptical shape and the specimen showed high fatigue strength, enough to reach the fatigue limit within tolerance of design stresses.

키워드

참고문헌

  1. Boiler and Pressure Vessel Code, Section XI, 1995, American Society of Mechanical Engineers, pp. 20-23
  2. Dreng, T., Robakowshi and Dreng, and Scierski, J. M., 1987, International Conference on Fatigue of Welded Constructions, England, Welding Institute, pp. 445-456
  3. Forrnan, R. G., 1972, 'Study of Fatigue Crack Initiation from Flaws Using Fracture Mechanics Theory,' Eng. Fract. Mech., Vol. 4, pp. 333-345 https://doi.org/10.1016/0013-7944(72)90048-3
  4. Lee, H. W. and Kang, S. W., 1997, 'A Study on Transverse weld Cracks in 50- mm Thick Steel Plate with the SAW Process,' Journal of Japan Welding Society, Vol. 15, No. 4, pp. 563-573 https://doi.org/10.2207/qjjws.15.563
  5. Lee, H. W., Kang, S. W. and Um, D. S., 1998, 'A Study on Transverse weld cRacks in Thick Steel Plate with the FCAW Process,' Welding Journal, Vol. 77, No. 12, pp. 503-510
  6. Lu, B., Zheng, X. and Li, D., 1993, 'Fatigue Crack Initiation and Propagation in Butt-Joint weld of an Ultrahigh-Strength Steel,' Welding Journal, Vol. 72, No. 2, pp. 79-86
  7. Structural Welding Code - Steel (ANSI/AWS D1.1-98) , American Welding Society, Miami, Fla., pp. 175-180
  8. Tsay, L. W., Chen, T. S., Gau, C. Y. and Yang, J. R., 1999, 'Microstructure and Fatigue Crack Growth of EH36 TMCP Steel weldments,' International Journal of Fatigue 21, pp. 857-864 https://doi.org/10.1016/S0142-1123(99)00021-3
  9. Yurioka, N., 1995, 'A Chart Method to Determine Necessary Preheat Temperature in Steel Welding,' Journal of Japan Welding Society, pp. 347-350 https://doi.org/10.2207/qjjws.13.347
  10. Zhang, M., Yang, P. and Tan, Y., 1999, 'Micromechanisms of Fatigue Crack Nucleation and Short Crack Growth in Low Carbon Steel Under Low Cycle Impact Fatigue Loading,' International Journal of Fatigue 21, pp. 823-830 https://doi.org/10.1016/S0142-1123(99)00031-6