초록
Dolomite type $BaSn(BO_3)_2$ ceramics with rhombohedral crystal structure has been synthesized via solid state reaction route. Dielectric properties were measured for the samples sintered at $1050\~1200^{\circ}C$ for 2 h in air. Dielectric constant, loss tangent, and temperature coefficient were increased with sintering temperature due to the evolution of $BaSnO_3$, secondary, phase. Optimum dielectric properties were obtained at the $BaSn(BO_3)_2$ ceramics sintered at $1100^{\circ}C.\;CuO/Bi_2O_3$ was added to $BaSn(BO_3)_2$ ceramics to lower the sintering temperature for LTCC application, then Co and Fe-based coloring agents were added for colorizing the LTCC tape. Typical dielectric properties of $BaSn(BO_3)_2$ ceramics with $5 wt\%\;CuO/Bi_2O_3\;and\;3wt\%$ Co-coloring agent that sintered at $900^{\circ}C$ were $\varepsilon_r=9.89,\;tan{\delta}=0.92\times10^{-3},\;and\;TCC=112ppm/^{\circ}C$. Thus obtained LTCC tape was co-fired with Ag paste for compatibility test and revealed no sign of Ag reaction with the ceramics.