La substituted perovskite $BiFeO_3$ have been prepared by a sol-gel method. Magnetic and structural properties of the powders were characterized with Mossbauer spectroscopy, XRD, SEM, and TG-DTA. The crystal structure is found to be a rhombohedrally distorted perovskite structure with the lattice constant $\alpha=3.985{\AA}\;and\;\alpha=89.5^{\circ}.\;Bi_{2/3}La_{1/3}FeO_3$ powders that were annealed at and above $600^{\circ}C$ have a single-phase perovskite structure. However, powders annealed at $900^{\circ}C$ have a typical perovskite structure with small amount of $Bi_2O_3$ phase. The Neel temperature of $Bi_{2/3}La_{1/3}FeO_3$ is found to be $680\pm3K$. The isomer shift value at room temperature is found to be 0.27 mm/s relative to the Fe metal, which is consistent with high-spin $Fe^{3+}$ charge states. Debye temperature far$Bi_{2/3}La_{1/3}FeO_3$ is found to be $305\pm5K$. The average hyperfine field $H_{hf}(T)$ of the $Bi_{2/3}La_{1/3}FeO_3$, shows a temperature dependence of $[H_{hf}(T)-H_{hf}(0)]/H_{hf}(0)=-0.42(T/T_N)^{3/2}-0.13(T/T_N)^{5/2}$ for $T/T_N<0.7$ indicative of spin-wave excitation.
[ $Bi_{2/3}La_{1/3}FeO_3$ ]분말을 졸-겔법을 이용하여 제조하였다. 결정학적 및 자기적 성질을 열분석장치(TG-DTA), x-선 회절분석기(XRD), 주사전자현미경(SEM) 및 Mossbauer분광기를 이용하여 연구하였다. $Bi_{2/3}La_{1/3}FeO_3$ 단일상은 $600^{\circ}C$에서 3시간 동안 공기 중에서 열처리하여 얻을 수 있었으며, x-선 회절분석 결과 $Bi_{2/3}La_{1/3}FeO_3$ 분말은 rhombohedral 형태로 변형된 단순 perovskite 구조를 가졌으며 이때 격자상수 $=3.985\pm0.0005{\AA},\;\alpha=89.5^{circ}$이었다. Mossbauer스펙트럼 분석결과 $Bi_{2/3}La_{1/3}FeO_3$의 Neel온도는 $680\pm3K$임을 알 수 있었다. $Bi_{2/3}La_{1/3}FeO_3$의 이성질체이동 값은 0.27mm/s 값을 가졌으며, 이는 $Bi_{2/3}La_{1/3}FeO_3$.의 Fe 이온이 가지는 이온가는 $Fe^{3+}$의 high spin상태임을 보여주었다. $Bi_{2/3}La_{1/3}FeO_3$의 결정내의 Debye 온도는 $305\pm5K$ 평균 초미세 자기장 $H_{hf}(T)$는 $T/T_N<0.7$영역에서 $[H_{hf}(T)-H_{hf}(0)]/H_{hf}(0)=-0.42(T/T_N)^{3/2}-0.13(T/T_N)^{5/2}$로 spin wave가 결정 내에서 잘 여기 됨을 알 수 있었다.