Anatomical and Physical Characteristics of Kenaf Grown in Korea

국내에서 생장한 Kenaf (양마)의 해부 및 물리적 특성

Anatomical and physical properties of kenaf grown in Chuncheon, Korea were investigated using light and scanning electron microscopy and X-ray diffraction method. Bast fiber, phloem ray, cortex parenchyma cell and sieve tube member were observed in phloem, and vessel element, fiber and ray in xylem. Solitary and multiple radial pores in xylem existed. The cell types of ray parenchyma in radial section were procumbent, upright and square cells. The length of bast fiber increased with increasing the growth period. The length of wood fiber was 0.74~0.82 mm, but was not significantly different between the growth period and stem height. Relative crystallinity was 53~74% in phloem and 43~58% in xylem. Cellulose crystallinity width was 2.68~3.24 nm in phloem and 2.46~2.95 nm in xylem. The green moisture content and green density increased but basic density decreased with increasing the stem height.

국내에서 재배된 케나프의 해부 물리적 특성을 광학현미경, 주사전자현미경 및 X선회절법으로 조사하였다. 그 결과 케나프는 사부에 인피섬유, 사부 방사조직, 피층 유세포, 사관요소 등이 존재하였고, 목부는 도관요소, 목섬유, 방사조직 등으로 구성되어 있었다. 관공은 고립 및 2~3개가 방사방향으로 복합한 것이 많이 존재하였고, 방사조직은 평복, 방형, 직립세포가 모두 분포하고 있었다. 수피부의 인피섬유 길이는 생장기간이 길어짐에 따라 점차 증가하였고, 목부 섬유의 길이는 평균 0.74~0.82 mm로써 생장기간과 줄기의 높이에 관계없이 거의 차이가 없었다. 상대결정화도는 사부가 53~74%, 목부가 43~58%인 것으로 나타났으며, 셀룰로오스의 결정폭은 사부가 2.68~3.24 nm, 목부가 2.46~2.95 nm 정도인 것으로 나타났다. 케나프 줄기의 높이가 증가함에 따라 생재함수율과 생재밀도는 증가하였으나, 기본밀도는 낮게 나타났다.